Tesis Doctoral
DOI
https://doi.org/10.11606/T.43.2002.tde-13122013-121304
Documento
Autor
Nombre completo
Sandro Martini
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2002
Director
Tribunal
Quivy, Alain Andre (Presidente)
Fantini, Marcia Carvalho de Abreu
Ferraz, Armando Corbani
Rodrigues, Wagner Nunes
Souza, Patrícia Lustoza de
Título en portugués
Estudo da segregação de Índio em camadas epitaxiais de In IND. X Ga IND. 1-X acrescidas sobre substratos de GaAs (001).
Palabras clave en portugués
Fotoluminescência
MBE
Poços quânticos
Segregação
Resumen en portugués
Neste trabalho, estudamos o crescimento epitaxial por feixe molecular assim como as propriedades ópticas e estruturais de camadas de InGaAs depositadas sobre substratos de GaAs(001) com diferentes ângulos e direções de corte. Um ênfase foi dada à investigação da segregação dos átomos de Índio que modifica consideravelmente o perfil de potencial das heteroestruturas e influencia as características dos dispositivos contendo este tipo de camadas. Um novo método experimental baseado em medidas de difração de elétrons de alta energia (RHEED) possibilitou a determinação in situ e em tempo real do coeficiente de segregação dos átomos de Índio e, conseqüentemente, do perfil de composição das camadas de InGaAs. Medidas de raios X e de fotoluminescência em baixa temperatura foram realizadas em amostras de poços quânticos de InGaAs e confirmaram, a posteriori, os resultados obtidos pela técnica RHEED. Foi também demonstrado que o uso de substratos desorientados podia reduzir levemente o efeito de segregação e melhorar as propriedades ópticas das camadas em baixa temperatura.
Título en inglés
Study of indium segregation in epitaxial layers of InxGa1-xAs added on GaAs substrates (001).
Palabras clave en inglés
MBE
Photoluminescence
Quantum wells
Segregation
Resumen en inglés
In this work, we investigated the molecular-beam-epitaxy growth as well as the optical and structural properties of InGaAs layers deposited on top of GaAs (001) substrates with different miscut angles and directions. We emphasized the investigation of the segregation of In atoms that considerably modifies the potential profile of the heterostructures and influences the characteristics of the devices based on this type of layers. A new experimental method involving the diffraction of high-energy electrons (RHEED) allowed the in-situ and real-time determination of the segregation coefficient of the In atoms and, consequently, of the compositional profile of the InGaAs layers. X-rays and low-temperature photoluminescence measurements were carried out InGaAs quantum wells and confirmed, a posterior, the results obtained by the RHEED method. It was also demonstrated that the use of vicinal substrates slight reduces the segregation effect and improves the optical properties of the layers at low temperature.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-02-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.