Master's Dissertation
DOI
https://doi.org/10.11606/D.43.2016.tde-07012016-121443
Document
Author
Full name
Vinicius Roberto de Sylos Cassimiro
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2015
Supervisor
Committee
Fantini, Marcia Carvalho de Abreu (President)
Gomes, Eliezer Ladeia
Salvadori, Maria Cecilia Barbosa da Silveira
Title in Portuguese
Zircônia céria mesoporosa para células de combustível e catalisadores
Keywords in Portuguese
Catalisadores
Dilatador de estrutura
Materiais nanoestruturados
Mesoporo
SOFC
Zircônia céria
Abstract in Portuguese
Os materiais à base de céria (CeO2) e zircônia (ZrO2) estão presentes em diversas aplicações tecnológicas, destacando-se como anodo de células de combustível de óxido sólido (SOFC) e em catálise, tanto para a produção de hidrogênio, como na automotiva (Three-Way Catalysis). A solução sólida ZrxCe1-xO2- é de especial interesse, pois apresenta melhor estabilidade térmica e maior capacidade de armazenamento de oxigênio (OSC), quando comparada com os óxidos não dopados. Os materiais mesoporosos (poros de 2 a 50 nm) possuem elevada área superficial e permeabilidade a gases, características estas importantes para o desempenho das SOFCs e dos processos de catálise. Neste trabalho, zircônia-céria (Zr0,1Ce0,9O2-) mesoporosa foi sintetizada pelo processo sol-gel, utilizando, como precursores, os cloretos inorgânicos (ZrCl4 e CeCl3.7H2O), o copolímero em bloco P123 (PEO20PPO70PEO20) como direcionador de estrutura e o TIPB (tri-isopropil-benzeno) como agente dilatador. A solução passou por tratamento hidrotérmico durante 48h a 80°C, com posterior calcinação a 400°C para a remoção do polímero, resultando no óxido cristalizado. Na análise foram utilizadas as técnicas: difração de raios X em alto ângulo (XRD), espalhamento de raios X a baixo ângulo (SAXS), isotermas de adsorção de nitrogênio (NAI) e microscopia eletrônica de varredura e transmissão (SEM e TEM). Os resultados mostraram que o material possui elevada área superficial (110m2/g), mesoporos de várias dimensões, atingindo valores médios em torno de 30 nm, fase majoritariamente cúbica Fm3m e, em menor proporção, tetragonal P42/nmc. As micrografias revelaram que o óxido está totalmente nano-cristalizado, com os poros tipo fendas e uma mesoporosidade secundária com distribuição de tamanhos menor e mais estreita. Quatro amostras foram sintetizadas com diferentes razões em massa TIPB/P123 (0, 1, 2 e 4), de forma que foi possível verificar um aumento na dimensão dos poros devido à inclusão do dilatador. As demais propriedades estruturais e morfológicas mantiveram-se inalteradas entre todas as amostras, mesmo com diferentes quantidades de TIPB.
Title in English
Mesoporous zirconia ceria for catalysts and fuel cells
Keywords in English
Catalysts
Mesopore
Nanostructured materials
SOFC
Swelling agent
Zirconia ceria
Abstract in English
The ceria (CeO2) and zirconia (ZrO2) based materials are present in several technological applications, mainly as Solid Oxide Fuel Cells (SOFC) anodes and catalysts, for hydrogen production and automotive converter (Three-Way Catalysis). The solid solution ZrxCe1-xO2- has attracted special attention, since it shows better thermal stability and higher oxygen storage capacity (OSC), if compared to the non-doped oxides. The mesoporous materials (pores of 2 to 50 nm) show high surface area and gas permeability, important properties for SOFCs and catalysts efficiency. In this work, mesoporous ceria-zirconia (Zr0,1Ce0,9O2-) was synthesized by a sol-gel route using inorganic chlorides (ZrCl4 e CeCl3.7H2O) as precursors, block copolymer P123 (PEO20PPO70PEO20) as template and TIPB (tri-isopropyl-benzene) as swelling agent. The solution was submitted to hydrothermal treatment for 48h at 80°C and calcined at 400°C to remove the template, resulting in the crystallized oxide. The characterization was performed by X-ray diffraction at high angles (XRD), small angle X-ray scattering (SAXS), nitrogen adsorption isotherms (NAI) and transmission and scanning electron microscopy (TEM and SEM). The results showed that the material has high surface area (110m2/g), a wide pore size distribution with mean values around 30 nm, predominant cubic phase Fm3m and, in less quantity, tetragonal P42/nmc. The micrographs revealed that the oxide is totally nano-crystallized, having pores with slit shape and a secondary smaller mesoporosity with a narrow size distribution. Four samples were produced with different TIPB/P123 mass rate (0, 1, 2, 4), therefore was possible to verify the pore size expansion due to the swelling addition. The structural and morphological properties remained unchanged, even with different quantities of TIPB.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2016-02-04
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2024. All rights reserved.