Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.43.2017.tde-03062017-212721
Document
Auteur
Nom complet
Thales Borrely dos Santos
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2017
Directeur
Jury
Chubaci, Jose Fernando Diniz (Président)
Mansano, Ronaldo Domingues
Rizzutto, Marcia de Almeida
Titre en portugais
Controle de propriedades de filmes finos de óxido de alumínio através da assistência de feixe iônico
Mots-clés en portugais
Al2O3
alumina
análise por feixe iônico
caracterização de lmes nos
IAB
IBAD
lmes nos
óxido de alumínio
Resumé en portugais
Este trabalho tem por objetivo a caracterização de filmes finos de óxido de alumínio produzidos por deposição assistida por feixe de íons Ar+. Tal caracterização consiste em estabelecer a relação entre os parâmetros de produção (energia do feixe e uxo relativo de Ar), a composição e a estrutura dos lmes. Para tanto, utiliza-se técnicas de microscopia de força atômica, difração de raios-x, reetividade de raios-x e análise por feixe iônico. Resultados mostram que amostras produzidas à temperatura ambiente e à 450 oC são amorfas independentemente da energia do feixe iônico. Filmes formados com assistência de feixe possuem qualidade superior àqueles formados por deposição física de vapor. O bombardeamento de íons Ar+ mostra-se capaz de controlar a concentração de hidrogênio, a estequiometria, a rugosidade, o tamanho dos grãos e a densidade dos lmes nos. Amostras com excelente qualidade baixa rugosidade, estequiometria próxima da ideal e boa densidade foram produzidas utilizando íons com energia dentre 300 eV e 600 eV.
Titre en anglais
Controlling aluminum oxide thin films properties through ion beam assistance.
Mots-clés en anglais
Al2O3
alumina
aluminum oxide
IAB
IBAD
ion assisted deposition
ion beam analysis
thin lm characterization
thin lms
Resumé en anglais
The scope of this work is the characterization of aluminum oxide thin films produced by Ar+ ion beam assisted deposition. This characterization consists in establishing the relationship between production parameters (ion beam energy and argon relative ux), structure and composition of these lms. In order to undertake this task, the following techniques were used: atomic force microscopy, x-ray diraction, x-ray reectivity and ion beam analysis. Results show that samples produced at room temperature and at 450 oC are amorphous regardless the ion beam energy. Films grown under ion assistance have better characteristics than the ones deposited by physical vapor deposition. The ion beam bombardment is capable of controlling hydrogen concentration, stoichiometry, roughness, grain size and density of alumina samples. High quality lms at surface and increased density lms with near ideal stoichiometry were produced with 300 eV and 600 eV ion beam energy.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2017-06-06
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.