• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Dissertação de Mestrado
Documento
Autor
Nome completo
Bianca Jardim Mendonça
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2018
Orientador
Banca examinadora
Chubaci, Jose Fernando Diniz (Presidente)
Silva, Antonio Ferreira da
Tatumi, Sonia Hatsue
Título em português
Produção e caracterização de filmes finos de TiO2
Palavras-chave em português
anatase
band gap
constante dielétrica
dióxido de titânio
magnetron sputtering
rutila
Resumo em português
Nesse trabalho foram fabricados filmes finos de TiO2 por RF magnetron sputtering reativo sobre substrato de silício (1 0 0). A pressão parcial do oxigênio na câmara foi variada de 5 a 100% em relação ao argônio. Após a deposição os filmes foram submetidos a tratamento térmico em atmosfera de oxigênio. A estequiometria dos filmes e o perfil de profundidade foram obtidos por RBS. A estrutura cristalina foi obtida por XRD. As propriedades ópticas foram obtidas por interferometria e reflectância e as elétricas por meio das curvas C-V. Os valores de espessura dos filmes sem tratamento térmico aumentaram aproximadamente 41% com o aumento do oxigênio na câmara de deposição. Essa variação está ligada ao aumento da eficiência do sputtering do alvo. Os índices de refração dos filmes sem tratamento térmico se mantiveram dentro de um intervalo de aproximadamente 2,3 a 2,4. A diminuição do band gap com o tratamento térmico é consequência da mudança de fase cristalográfica de anatase para rutila. A estequiometria TiOx dos filmes antes do tratamento térmico apresentaram valores de x entre 2,0 e 2,4. A espessura em TFU dos filmes aumentou com o percentual de oxigênio na câmara. As amostras que receberam tratamento térmico apresentaram difusão de titânio na interface do substrato e incorporação de oxigênio no filme. Os valores da constante dielétrica aumentaram com o percentual de oxigênio na câmara, em contraposição com o efeito do tratamento térmico que diminuiu o valor. Todos os resultados observados são coerentes do ponto de vista da mudança de fase anatase rutila e aumento do percentual de oxigênio na câmara.
Título em inglês
Production and Characterization of TiO2 Thin Films
Palavras-chave em inglês
anatase
band gap
dielectric constant
magnetron sputtering
rutile
titanium dioxide
Resumo em inglês
In this work thin films of TiO2 were produced by reactive RF magnetron sputtering on silicon substrate (1 0 0). The oxygen partial pressure in the chamber was varied from 5 to 100% in relation to argon. After deposition the films were submitted to thermal treatment under an oxygen atmosphere. The stoichiometry of the films and the depth profile were obtained by RBS. The crystal structure was obtained by XRD. Its optical properties were obtained by interferometry and reflectance and the electrical were obtained by means of the C-V curves. The thickness values of films without heat treatment increased approximately 41% with the increase of oxygen in the deposition chamber. This variation is linked to the increased sputtering efficiency of the target. The refractive indexes of films without heat treatment remained within a range of about 2.3 to 2.4. The decrease of the band gap with the heat treatment is a consequence of the change of crystallographic phase from anatase to rutile. The TiOx stoichiometry of the films before the heat treatment showed values of x between 2.0 and 2.4. The TFU thickness of the films increased with the percentage of oxygen in the chamber. The samples that received heat treatment shows diffusion of titanium at the interface of the substrate and incorporation of oxygen in the film. The values of the dielectric constant increased with the percentage of oxygen in the chamber, as opposed to the effect of the thermal treatment that decreased the value. All the results observed are consistent from the point of view of the anatase - rutile phase transition and the increase in the oxygen percentage in the chamber.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2018-05-04
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.