Doctoral Thesis
DOI
10.11606/T.3.2011.tde-12122011-141235
Document
Author
Full name
John Ferney Alvarez Rosario
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2011
Supervisor
Committee
Machado, Izabel Fernanda (President)
Batalha, Gilmar Ferreira
Grijalba, Freddy Armando Franco
Hassui, Amauri
Neves, Julio Cesar Klein das
Title in Portuguese
Estudo da integridade superficial e seu efeito na fadiga de contato de um aço ferramenta.
Keywords in Portuguese
Fadiga de contato de rolamento
Integridade superficial
Retificação
Torneamento
Abstract in Portuguese
Os processos de manufatura, bem como os parâmetros de processamento utilizados produzem diferentes resultados com relação à integridade de uma superfície. Estas alterações se refletem em mudança das propriedades da superfície, as quais podem influenciar o desempenho dos componentes. O presente trabalho estuda o efeito da integridade superficial gerada pelos processos de torneamento e retificação na resistência à fadiga de contato do aço ferramenta AISI H13. A influência do processo de usinagem e dos parâmetros de corte no estado da superfície e subsuperfície, e como estas características afetam o desempenho são determinados. Foram geradas quatro condições diferentes para as superfícies torneadas mediante a combinação de parâmetros de corte. As superfícies retificadas foram produzidas empregando as mesmas condições de retificação, com isso, obteve-se a mesma condição para todos os corpos de prova ensaiados. As características medidas da integridade superficial foram: os parâmetros de rugosidade, tensões residuais, microdureza Vickers da seção transversal e ruído magnético de Barkhausen. Foi determinado o desempenho das superfícies por fadiga de contato de rolamento, num equipamento na configuração esfera-plano. Os corpos de prova foram anéis de AISI H13 temperados e revenidos. A totalidade dos ensaios foi realizada até a ocorrência de lascamento (Spalling). Os ensaios foram realizados com lubrificação e com uma máxima pressão de contato de Hertz de 3,6 GPa. Foi observado que dependendo do nível de integridade superficial induzido pelo processo de usinagem e dos parâmetros selecionados, o desempenho da superfície em fadiga de contato de rolamento foi afetado. Contudo, as melhores condições de desempenho foram dos materiais retificados, e para os materiais torneados o melhor desempenho foi obtido com maiores velocidades de corte.
Title in English
The effect of surface integrity on the contact fatigue resistance of a tool steel.
Keywords in English
Grinding
Rolling contact fatigue
Surface integrity
Turning
Abstract in English
The manufacturing process and the machining parameters selected lead to different integrity of the surface, and these characteristics will influence the functional performance of the components. This study evaluated and analyzed the effect of surface integrity on the contact fatigue resistance of the H13 hot work tool steel. The surfaces were manufactured by hard turning and grinding process. Therefore, the influences of the machining process and the cutting parameters on the surface and on the subsurface layer were studied. Four different turned surfaces were obtained as a combination of cutting parameters selected for the tests. On the other hand, grinding surfaces were generated using the same machining conditions. The characteristics of surface integrity evaluated were: surface roughness parameters, residual stresses, Barkhausen noise, and microhardness of surface and sub-layers in transverse section. It was also evaluated the performance of the samples by rolling contact fatigue tests conducted in a ball on washer machine. The specimens were rings made of AISI H13 steel, which were quenched and tempered. All tests were performed until the occurrence of spalling. The tests were carried out under lubrication and with a maximum Hertz contact pressure of 3.6 GPa. Monitoring and failure detection were carried out by analyzing the changes in the vibration signal of the test machine sensors. It was observed that the performance of the surface in rolling contact fatigue resistance was affected by the level of the surface integrity, related to the machining process and the machining parameters.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2011-12-15
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2019. All rights reserved.