Dissertação de Mestrado
Documento
Autor
Nome completo
Alessandra Piaia
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2017
Orientador
Banca examinadora
Mierzwa, José Carlos (Presidente)
Diaz, Francisco Rolando Valenzuela
Souza, Juliana dos Santos de
Título em português
Síntese e caracterização de membrana condutiva para tratamento de água e efluentes.
Palavras-chave em português
Efluentes (Tratamento)
Tratamento de água
Resumo em português
Neste trabalho, foram adicionadas diferentes concentrações de polianilina (PANI) a uma solução polimérica de poliétersulfona (PES) e N-metil-pirrolidona (NMP), com o intuito de sintetizar membranas de ultrafiltração a partir do método de inversão de fases. O desafio consistem em combinar alta condutividade elétrica, boas propriedades mecânicas e oxidação eletroquímica, permitindo assim que a oxidação de possíveis contaminantes ocorra ao mesmo tempo em que a membrana atua como uma barreira de filtração seletiva. O efeito da adição de PANI foi avaliado quanto à morfologia da membrana, capacidade de separação e desempenho, em termos de permeabilidade e condutividade. As membranas modificadas apresentaram uma morfologia muito singular quando analisadas pelo Microscópio Eletrônico de Varredura (MEV), poros maiores foram identificados, ausência da camada seletiva, diminuição da camada inferior e grandes fases aglomeradas ao longo da seção transversal. Devido ao aumento do tamanho dos poros, a seletividade das membranas modificadas foi comprometida. Os resultados de porosidade para as membranas modificadas variaram entre 53 e 66%. A permeabilidade e a condutividade das membranas modificadas aumentaram à medida que a concentração de PANI também aumentou. O fluxo mediano obtido para a membrana com concentração de 40% de PANI foi de 835 L.m-2.h-1, cerca de 5 vezes maior do que o fluxo mediano obtido para a membrana controle. Já a condutividade mediana obtida para a mesma membrana modificada foi de 1,7x10-6 S, cerca de 15 vezes maior do que a membrana controle. Durante o teste de voltametria cíclica não foram observadas reações de oxidação-redução, nem da solução de ferro-cianeto nem da própria polianilina, ao aplicar uma tensão variando entre -0,2 V e 0,8 V. Desta forma, a partir dos resultados, pode-se afirmar que a adição de Polianilina alterou a morfologia e o desempenho das membranas modificadas, destacando o incremento na permeabilidade, hidrofilicidade e condutividade, mantendo sua característica de ser uma barreira de filtração seletiva.
Título em inglês
Synthesis and characterization of conductive membrane for water and waste water treatment.
Palavras-chave em inglês
Conductive membrane
Performance
Polyaniline
Polyethersulfone
Resumo em inglês
In this work, different concentrations of Polyaniline (PANI) were added to a polymer solution made of Polyethersulfone (PES) and N-methylpyrrolidone (NMP), in order to synthesize ultrafiltration membranes by the phase inversion method and the challenge of combine high electrical conductivity, good mechanical properties and electrochemical oxidation, thus allowing the oxidation of matter to occur at the same time that the membrane acts as a selective and reliable filtration barrier. The effect of PANI addition was evaluated regarding the membrane morphology, separation capacity and performance in terms of permeability and conductivity. The modified membranes presented a very unique morphology when analyzed by the Scanning Electron Microscope (SEM), larger pores were identified, absence of the selective layer, decrease of the lower layer and large agglomerated phases with phase contour characterization along the cross section. Due to the increase in pore size, the selectivity of the modified membranes was compromised. The porosity results for the modified membranes are only reflections of the morphology obtained, and the median porosities varied between 53 and 66%. The permeability and conductivity of the modified membranes increased as the PANI concentration also increased. The median flow obtained for the membrane with 40% PANI concentration was 835 L.m-2.h-1, about 5 times higher than the median flow obtained for the control membrane. The median conductivity obtained for the same modified membrane was 1.7x10-6 S, about 15 times higher than the control membrane. During the cyclic voltammetry test, no oxidation-reduction reactions were observed, neither the iron-cyanide solution nor the polyaniline itself, when applying a voltage ranging from -0.2 V to 0.8 V. From the results, it can be affirmed that the addition of polyaniline particles altered the morphology and performance of the modified membranes, highlighting the increase in permeability, hydrophilicity and conductivity, maintaining its characteristics of being a selective filtration barrier.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2017-11-10
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2014. Todos os direitos reservados.