• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Dissertação de Mestrado
DOI
10.11606/D.3.2006.tde-17112006-141646
Documento
Autor
Nome completo
Rosiany da Paixão Silva
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2006
Orientador
Banca examinadora
Barros, Mercia Maria Semensato Bottura de (Presidente)
Gleize, Philippe Jean Paul
John, Vanderley Moacyr
Título em português
Argamassas com adição de fibras de polipropileno -estudo do comportamento reológico e mecânico.
Palavras-chave em português
Argamassa para revestimento
Fibra de polipropileno
Reologia
Resistência mecânica
Revestimento de argamassa
Trabalhabilidade
Resumo em português
Buscando evitar as anomalias surgidas nos revestimentos de argamassa, muitos projetistas e construtores têm procurado soluções alternativas, dentre as quais aparece o emprego de argamassas com adição de fibras. Porém, o conhecimento sobre o comportamento deste compósito é empírico, principalmente no Brasil, onde inexistem pesquisas sistêmicas sobre o assunto. A partir deste contexto, o presente trabalho teve por objetivo investigar a influência da adição de fibras de polipropileno em argamassas para revestimento, no que se refere ao seu comportamento reológico e mecânico. Para avaliar o comportamento reológico, foram empregadas as técnicas de ensaio dropping ball e squeeze flow, e a avaliação da aplicabilidade quanto à execução do revestimento, utilizando o conhecimento de um operário experiente. Para avaliar o comportamento mecânico, foram utilizados ensaios relativos a resistência à tração na flexão, resistência à compressão e módulo de elasticidade dinâmico. Os compósitos de argamassa produzidos no trabalho apresentam variação na matriz e no teor de fibras. A variação na matriz compreendeu o tipo de argamassa e a dosagem de água. Foram utilizadas duas argamassas, largamente empregadas no mercado da Construção Civil, uma com baixo teor de ar incorporado (da ordem de 5%) e outra com alto teor (da ordem de 30%) e foram utilizados seis teores de água. Quanto à fibra, empregou-se um único tipo, com 6mm de comprimento, variando-se o seu teor na mistura, com cinco dosagens distintas. Como resultado, constatou-se que a adição de fibras influencia na reologia das argamassas devido (não somente) às suas características físicas e mecânicas, mas também porque ao serem introduzidas, modificam fortemente as características da matriz original, como por exemplo, as alterações do teor de ar incorporado. Assim, constatou-se que a adição de fibras na argamassa com baixo teor de ar elevou este teor; enquanto na com alto teor de ar, a adição de fibras reduziu o teor de ar. Estas alterações conferiram condições de aplicabilidade particulares a cada tipo de argamassa. O comportamento mecânico das argamassas também foi alterado. Dentre os “modificadores reológicos” estudados, o teor de fibras na argamassa com baixo teor de ar incorporado foi o que mais contribuiu com a alteração da propriedade mecânica; enquanto para a argamassa com alto teor de ar, o teor de água é o que mais afeta o comportamento mecânico.
Título em inglês
Mortars with polypropylene fibres´addition - study of the rheological and mechanical behavior.
Palavras-chave em inglês
Mechanical resistance
Mortar for the rendering
Mortar rendering
Polypropylene fibers
Rheological and mechanical behavior
Resumo em inglês
Many designers and constructors have been looking for alternative solutions trying to avoid types of anomalies in the mortar rendering. One of these solutions is the application of mortar with fibres’ addition. However, the knowledge concerning the composite behavior is very empirical, mainly in Brazil where there are no systematic researches about this subject. From this context, the objective of this job is to investigate the influence of the polypropylene fibres’ addition in the rheological and mechanical behavior of the mortar applied in rendering. For the study of the rheological behavior, laboratory evaluations were done using the following methods: dropping ball and squeeze flow. Furthermore, for the applicability evaluation, the knowledge of an expert was taken into account. For the study of the mechanical behavior, laboratory evaluations were done using the following methods: evaluation of the flexural strength, compressive strenght and dynamic elastic modulus. In this job, the mortar composites present variation in the matrice and fibre. The variation in the matrice involves the mortar type and the water dosage. Two mortars widely used in the civil construction market were used in this present work: one with low air voids formation (about 5%) and other with high air voids formation (about 30%). Six water percentages were also used in the matrice variation. Polypropylene fibres with length 6mm were used in the fibre variation. Five different fibre percentages were used in the mixes. As results, the fibres’ addition evidenced alterations in the mortars rheological due (not only) to physicals and mechanicals characteristics, but also because when the fibres were inserted, they modified the characteristics of the original matrice strongly, as for example, the alteration of the incorporated air percentage. So, the fibres’ addition in the mortar with low air voids formation increased the air formation; while in the mortar with high air voids formation, the fibres’ addition decreased the air formation. These alterations evidenced the specifics applicability conditions for each type of mortar. The mortar mechanical behavior also was altered. Inside the “rheological modifications” studied, the fibre percentage in the mortar with low air voids formation was what more contributed with the alteration of the mechanical property; while that the mortar with high air voids formation, the water percentage is what more affected the mechanical behavior.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2006-12-19
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.