• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Dissertação de Mestrado
DOI
10.11606/D.3.2008.tde-25092008-140736
Documento
Autor
Nome completo
Fernando Trevisan Saez Parra
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2008
Orientador
Banca examinadora
Santos Filho, Sebastião Gomes dos (Presidente)
Lucchi, Júlio César
Onmori, Roberto Koji
Título em português
Fabricação e caracterização de termopares Cu/CuNixPy obtidos por deposição eletroquímica.
Palavras-chave em português
Eletrodeposição
Filmes finos
Sensor
Resumo em português
Neste trabalho foram estudadas deposições químicas de ligas CuNixPy e foram fabricados termopares Cu/CuNixPy sobre superfícies de lâminas de silício. Inicialmente, as superfícies foram pré-ativadas em uma solução diluída de ácido fluorídrico contendo PdCl2. Em seguida, foi empregado um banho químico alcalino diluído em água deionizada contendo 15 g/l NiSO4.6H2O; 0,1 a 0,3 g/l CuSO4.5H2O; 15 g/l Na2HPO2.H2O e 60 g/l Na3C6H5O7.2H2O na temperatura de 80OC sendo que NH4OH foi adicionado até que o pH do banho atingisse o valor de 8,0. Verificamos que a concentração do sal de cobre na solução de deposição afeta substancialmente a quantidade de cobre nos depósitos de CuNixPy. As concentrações planares e as composições dos filmes depositados foram obtidas através da técnica de espectrometria de retroespalhamento de Rutherford (RBS) e a morfologia superficial foi caracterizada através da técnica de microscopia de força atômica (AFM). A solução: 15 g/l NiSO4.6H2O + 0,3 g/l CuSO4.5H2O + 15 g/l Na2HPO2.H2O + 60 g/l Na3C6H5O7.2H2O + NH4OH (pH 8.0) na temperatura de 80OC foi a escolhida na obtenção da liga CuNiP0,5 para a construção de termopares Cu/CuNiP0,5 os quais apresentaram potência termoelétrica de aproximadamente (866) V/oC semelhante aos valores típicos apresentados na literatura para Cu/CuNi.
Título em inglês
Fabrication and characterization of Cu/CuNixPy thermocouples obtained by electroless deposition.
Palavras-chave em inglês
Electroless deposition
Thermocouple
Thermoelectric power
Resumo em inglês
In this work, it was studied chemical depositions of CuNixPy alloys and it was fabricated Cu/CuNixPy thermocouples onto silicon wafer surfaces. Initially, surfaces were pre-activated in a diluted hydrofluoric acid solution containing PdCl2. Following, it was used a de-ionizedwater- diluted alkaline chemical bath containing 15 g/l NiSO4.6H2O; 0,1-0,3 g/l CuSO4.5H2O; 15 g/l Na2HPO2.H2O and 60 g/l Na3C6H5O7.2H2O at temperature of 80OC where NH4OH was added until ph was 8.0. The concentration of copper salt in the deposition solution greatly affected the Cu content of the CuNixPy deposits. Areal concentration and composition were measured by Rutherford Backscattering Spectrometry (RBS) and surface morphology was characterized by Atomic Force Microscopy (AFM). The solution: 15 g/l NiSO4.6H2O; 0.3 g/l CuSO4.5H2O; 15 g/l Na2HPO2.H2O; 60 g/l Na3C6H5O7.2H2O; NH4OH (pH 8.0) at the temperature of 80OC was chosen to obtain the CuNiP0.5 alloy to fabricate Cu/CuNiP0.5 thermocouples with thermoelectric power of about (866) V/oC, which is similar to the typical values reported in literature for Cu/CuNi.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
CapaseIndices.pdf (68.83 Kbytes)
Dissertacao.pdf (2.12 Mbytes)
Data de Publicação
2008-10-07
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2019. Todos os direitos reservados.