Disertación de Maestría
DOI
https://doi.org/10.11606/D.3.2008.tde-11052009-170655
Documento
Autor
Nombre completo
Ary Adilson Morales Alvarado
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2008
Director
Tribunal
Pereyra, Inés (Presidente)
Fantini, Márcia Carvalho de Abreu
Mansano, Ronaldo Domingues
Título en portugués
Estudo e caracterização de filmes de a-Si1-xCx:H obtidos por PECVD visando sua aplicação em MEMS e dispositivos ópticos.
Palabras clave en portugués
Dispositivos ópticos
Filmes finos
Processos de microeletrônica
Sistemas microeletromecânicos
Resumen en portugués
Neste trabalho foi desenvolvido um estudo sistemático das propriedades estruturais, mecânicas e ópticas de filmes de carbeto de silício amorfo hidrogenado (a-Si1-xCx:H) produzidos pela técnica de deposição química a vapor assistida por plasma (PECVD) a baixas temperaturas (320°C), utilizando silana (SiH4) e metano (CH4) como gases precursores do silício e carbono, com a finalidade de avaliar sua aplicabilidade em processos de microfabricação. Foram depositadas duas séries de filmes de a-Si1-xCx:H, com e sem diluição de hidrogênio da mistura gasosa, variando alguns parâmetros, como potência de RF, concentração de metano e fluxo de silana. Os filmes depositados com a mistura gasosa diluída em hidrogênio apresentaram valores maiores de módulo de elasticidade, dureza, gap óptico e índice de refração, comparados com os filmes depositados sem a adição de hidrogênio; no entanto esses filmes apresentaram também valores maiores de stress residual, ocasionando deformações e em alguns casos a quebra das microestruturas fabricadas. No caso das amostras depositados sem a adição de hidrogênio na mistura gasosa, os filmes com conteúdo de carbono maior que 45% depositados com baixa densidade de potência (50 mW.cm-2) apresentaram baixos valores de stress residual compressivo (menores que 60 MPa) e, as microestruturas fabricadas com eles mostraram que o material possui uma superfície livre de defeitos e uma excelente aderência ao substrato, mostrando a viabilidade de poder utilizá-lo como material estrutural e de mascaramento em processos de microfabricação. Além disso, esses filmes são transparentes para comprimentos de onda acima de 600 nm na região visível do espectro eletromagnético, apresentando-o como um material promissório para a fabricação de guias de onda. Finalmente, com o incremento da potência de RF para 100 W na deposição do filme quase estequiométrico com a mistura gasosa não diluída em hidrogênio, conseguiu-se duplicar a taxa de deposição para aproximadamente 12 nm/min, incorporando uma maior quantidade de carbono (~57%), porém também aumento o valor do stress residual compressivo para ~267 MPa. No entanto, as estruturas suspensas fabricadas com este material não apresentaram deformações notáveis.
Título en inglés
Study and characterization of a-Si1-xCx:H thin films produced by PECVD aiming applications in mems and optical devices.
Palabras clave en inglés
MEMS
Microeletronic processes
Optical devices
Thin films
Resumen en inglés
In this work a study of structural, mechanical and optical properties of hydrogenated amorphous silicon carbide (a-Si1-xCx:H) films, obtained by plasma enhanced chemical vapor deposition (PECVD) at low temperatures (320°C), using silane (SiH4) and methane (CH4) as a gaseous precursors of silicon and carbon, respectively is performed, intending to assess their suitability in microfabrication processes. Two series of a-Si1-xCx:H films were deposited, with and without hydrogen dilution of the gaseous mixture, varying parameters, such as RF power, methane concentration and silane flow. The films deposited with hydrogen diluted gaseous mixture showed higher values of elastic modulus, hardness, optical gap and refractive index, compared with films produced without hydrogen dilution; however these films present higher values of compressive residual stress, causing deformations and in some cases cracks in the microstructures utilizing these films as structural material. In the case of the films deposited without hydrogen dilution of the gaseous mixture, those with carbon contents higher than 45% deposited at low power densities (50 mW.cm-2) presented lower values of compressive residual stress (lower than 60 MPa), and the microstructures fabricated with these materials do not show defects in the surface and have a good adherence to the substrate, demonstrating the feasibility of using these materials as structural and masking materials in microfabrication processes. Moreover, these samples are transparent to wavelengths larger than 600 nm in the visible range of the spectrum, making it suitable to the fabrication of waveguides. Finally, with the increase in the RF power to 100 W in the deposition process without hydrogen dilution a sample close to stoichiometry presented an increase in the deposition rate to approximately 12 nm/min and in the carbon content (~57%); however the compressive residual stress also increased. In spite of that, the microstructures fabricated with this material do not show notable deformations.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-07-03
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.