Doctoral Thesis
DOI
10.11606/T.3.2010.tde-25102011-175019
Document
Author
Full name
Marjorie Benegra
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2010
Supervisor
Committee
Goldenstein, Hélio (President)
Kunioshi, Clarice Terui
Oliveira, Ana Sofia Clímaco Monteiro de
Silva, Wanderson Santana da
Souza, Roberto Martins de
Title in Portuguese
Desenvolvimento "in situ" de aluminetos de níquel por plasma por arco transferido resistentes à oxidação.
Keywords in Portuguese
Aluminetos de níquel
Estabilidade microestrutural
Intermetálicos
Oxidação
Plasma por Arco Transferido (PTA)
Abstract in Portuguese
O presente trabalho objetiva o desenvolvimento in situ por plasma por arco transferido (PTA) de aluminetos de Níquel resistentes à oxidação, baseados em uma liga NiCrAlC referência. Para tanto, foram depositadas misturas preliminares de pós elementares e também utilizando o pó atomizado, variando somente a intensidade de corrente (130 e 160 A) para se obter diferentes misturas com o substrato. Após as deposições, a incorporação de elementos do substrato nos cordões não permitiu a formação de aluminetos para os revestimentos processados com a mistura de pós elementares. Estes apresentaram valores de diluição consideravelmente maiores do que os cordões obtidos com pó atomizado, que resultaram em aluminetos de Níquel. Com base nos resultados preliminares, quatro novas composições com mistura de pós elementares foram estimadas e os cordões finais, processados com 100 ou 130 A, resultaram em aluminetos como esperado. Duas composições foram submetidas a ensaios em balança termo gravimétrica (TGA) e a ciclos isotérmicos em forno mufla para diferentes temperaturas (máximo de 1000 graus Celsius) e tempos de exposição (até 72 horas no máximo). Os resultados mostraram que a incorporação de Ferro nos revestimentos durante a deposição retardou a formação das camadas de óxidos, sendo que maiores teores deste elemento aceleraram a formação da camada de alumina alfa, o que propiciou uma redução nos valores de constante de oxidação parabólica a 1000 graus Celsius nos estágios iniciais da oxidação. Os revestimentos apresentaram melhores desempenhos à oxidação do que a liga NiAlCrC fundida, traduzido pelo menor ganho de massa. A exposição nas temperaturas de ensaio provocou uma queda de dureza e na evolução ou nucleação de uma provável fase sigma.
Title in English
Development "in situ" of nickel aluminides by plasma transferred arc resistant to the oxidation.
Keywords in English
Intermetalics
Microstructural stability
Nickel aluminides
Oxidation
Plasma Transferred Arc (PTA)
Abstract in English
This research aimed at the development in situ by plasma transferred arc (PTA) of nickel aluminides resistant to the oxidation, based on a reference NiCrAlC alloy. For this purpose, preliminary mixtures of elemental powders were deposited, and also using the atomized powder, varying the current intensity (130 and 160 A) only to obtain different mixtures with substrate. After the depositions, the incorporation of substrate elements into the welds did not allow the formation of aluminides in the coatings processed with the elemental powder mixture. These coatings presented dilution values considerably higher than those obtained with atomized powder, which result in nickel aluminides. Based on the preliminary results, additional four compositions with elemental powders were estimated and the final welds, processed with 100 or 130 A, were composed by aluminides as expected. Two compositions were submitted to the thermogravimetry tests and isothermal cycles in an oven for different temperatures (1000 Celsius max) and exposure times (for 72 hours at maximum). The results showed that the iron incorporation in the coatings during depositions delayed the oxides scales formation, since higher contents of this element accelerated the formation of -alumina, which promoted a reduction in the parabolic constant of oxidation for 1000 Celsius in the earlier stages of oxidation. The coatings presented better oxidation resistance than that observed for as-cast NiCrAlC, observed by their smaller mass losses. The exposure to the testing temperatures resulted in a decrease of hardness and in the evolution or nucleation of sigma phase.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2011-10-26
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2019. All rights reserved.