Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.3.2001.tde-21072006-102226
Document
Auteur
Nom complet
Wanderson Santana da Silva
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2001
Directeur
Jury
Goldenstein, Helio (Président)
Bastian, Fernando Luiz
Falleiros, Ivan Gilberto Sandoval
Titre en portugais
Estudo da tenacidade à fratura do aço rápido M2 fundido, modificado e tratado termicamente.
Mots-clés en portugais
aço rápido M2 fundido
carbonetos eutéticos
elementos modificadores
ensaio chevron
tenacidade à fratura
tratamentos térmicos de decomposição
Resumé en portugais
Neste trabalho foi medida a tenacidade à fratura de quatro ligas fundidas com composição química base do aço AISI M2 – uma de composição química convencional (liga I), e as demais modificadas por adições de nitrogênio (liga II), cério (liga III) e antimônio (liga IV) – submetidas a tratamentos térmicos visando a decomposição do carboneto M2C, a esferoidização e engrossamento dos carbonetos produto M6C e MC, em altas temperaturas e por diversos tempos. A metodologia empregada nesta avaliação da tenacidade à fratura foi a dos corpos de prova curtos com entalhe chevron segundo ASTM E 1304-97, de forma a superar a necessidade do pré-trincamento por fadiga, procedimento de difícil controle e custoso em materiais como os aços rápidos temperados e revenidos. Verificou-se que a metodologia utilizada para obtenção e ensaio de corpos de prova chevron foi de fácil execução (comparada à metodologia convencional) permitindo grande número de experimentos. Para verificar a consistência dos resultados, em algumas condições, também se utilizou a metodologia convencional segundo a ASTM E 399-90, cujo pré-trincamento foi feito utilizando os procedimentos propostos por Harris e Dunegan. Os resultados obtidos para os aços fundidos foram correlacionados com os obtidos para outros aços rápidos convencionais (VM2, M2 Thyssen) e um aço rápido sinterizado (SINTER 23). A microestrutura foi caracterizada utilizando-se técnicas de ataques metalográficos diferenciais, metalografia quantitativa manual e computadorizada e microscopia eletrônica de varredura. A avaliação microestrutural indica que não ocorreu precipitação eutética do carboneto M6C, em nenhuma das ligas fundidas. O carboneto M2C apresenta morfologia tanto irregular (plaquetas – tipo 1) quanto regular-complexa (lamelas – tipo 2). As ligas I, III e IV, apresentaram a predominância da morfologia tipo 1 enquanto que a liga II modificada pelo nitrogênio, apresentou apenas a morfologia tipo 2. O carboneto MC apresentou-se com morfologia regular-complexa. Medidas do espaçamento interdendrítico indicam que não houve influência significativa dos elementos modificadores sobre este parâmetro. Ensaios de resistência à flexão, indicam pouca influência dos elementos modificadores, mas forte influência dos tratamentos térmicos sobre o limite de resistência à ruptura transversal do aço fundido. Em todas as ligas, a resistência à flexão cresceu com o tempo de tratamento a 1200°C, bem como com a temperatura de decomposição em tratamentos por 2 horas. Análise das fraturas por microscopia eletrônica de varredura indicou que o crescimento das trincas se deu na região interdendrítica. O aço convencional apresentou resistência à ruptura transversal muito superior à dos aços fundidos. Os ensaios de tenacidade à fratura apresentaram resultados compatíveis com a literatura para os aços AISI M2 convencional e SINTER 23. Os resultados obtidos para o aço fundido, indicam queda nos valores de tenacidade à fratura nos materiais tratados a 1050°C com o avanço do tempo de tratamento; pouca variação dos valores com o tempo nas amostras tratadas a 1150°C; e aumento significativo da tenacidade à fratura com o tempo de tratamento a 1200°C. Os valores de tenacidade obtidos para os aços rápidos fundidos foram mais elevados que os obtidos para os materiais trabalhados e para o material sinterizado.
Titre en anglais
Fracture toughness of as-cast high speed steel M2, modified and heat treated.
Mots-clés en anglais
as-cast M2 high speed steel
chevron notch
decomposition heat treatments
eutectic carbides
fracture toughness
modifiers elements
Resumé en anglais
Fracture Toughness of four cast alloys with chemical composition based on the High-Speed Steel AISI M2 were measured. One of the alloys (alloy I) had the conventional AISI M2 composition, while the other three were modified by the addition of N (alloy II), Ce (alloy III) and Sb (alloy IV). The cast alloys were heat-treated in order to promote the decomposition of the M2C carbide as well as spheroidize and coarsen the product M6C e MC carbides. The method chosen for measuring fracture toughness was based on the use of short rod and bar chevron notched samples, according to ASTM E1304 – 97, in order to evade the need for fatigue pre-cracking, notoriously difficult for High Speed Steels quenched and tempered. The chevron-notch method proved straightforward and allowed for successful testing a great number of specimens. Conventional compact sample fracture toughness, according to ASTM E 399-90, with pre-cracking obtained using Harris-Dunegan drop-weight procedure, was used to validate the results. The results for cast alloys were compared with conventionally produced High Speed Steels (VM2, M2 Thyssen) and with a powder metallurgy High Speed Steel (SINTER 23). Microstructural characterization was performed using selective etching of polished surfaces, manual and automated quantitative metallography and SEM. Microstructural evaluation of as-cast alloys showed that there was no eutectic precipitation of M6C carbides. The M2C carbides show an irregular eutectic morphology (Type 1- plates) as well as a regular-complex eutectic morphology. Measurements of interdendritic spacing did not detect any effect of the modification. The bending test rupture strengths did not vary with the addition of modifying elements, but increased with the time and temperature of decomposition, spheroidization and coarsening of carbides. Rupture strengths increased with the heat-treatment time at 1200°C as well as with increasing temperatures for 2 h heat-treatments. SEM examination of the fracture surfaces showed that crack preferential growth path was interdendritical. Conventional High Speed Steels tested in bending presented better results for the rupture strength than cast steels. Fracture toughness results for M2 conventional steels and for the SINTER 23 steel were similar to the results from the literature. Fracture toughness results obtained for cast steels diminished with increasing decomposition time at 1050°C, did not change much with increasing decomposition time at 1150°C, increased markedly withy increasing decomposition times at 1200°C. The fracture toughness results for the as-cast steels were higher than the results obtained for the wrought steels and for the powder metallurgy steel.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2006-07-24
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.