Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.3.2011.tde-20032012-110351
Document
Auteur
Nom complet
Marcos Machado Matsumoto
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2011
Directeur
Jury
Goldenstein, Hélio (Président)
Albertin, Eduardo
Serantoni, Claudia Regina
Titre en portugais
Estudo sobre a resistência à ciclagem térmica dos ferros fundidos de alto cromo e do aço ferramenta AISI D2.
Mots-clés en portugais
Aço ferramenta AISI D2
Ciclagem térmica
Ferro fundido branco de alto cromo
Resumé en portugais
Este estudo apresenta uma abordagem para a avaliação do comportamento de um ferro fundido branco de alto cromo e um aço ferramenta AISI D2 submetido a ciclos térmicos. Para a realização do estudo foi desenvolvido um procedimento para ensaios de fadiga térmica submetidos a números de ciclos variados, usando para aquecimento um sistema indutivo e para resfriamento um tanque de água. Devido a complexidade dos fenômenos envolvidos, um modelo de elementos finitos foi elaborado para a solução do campo de temperaturas e tensões superficiais atuantes. O controle da tensão superficial atuante foi realizado por meio da mudança de geometria do corpo de prova, sendo esta geometria resultante de teste por simulação computacional. Os corpos de prova foram caracterizados quando a sua microdureza e fração volumétrica de carbonetos antes do ensaio e após ensaio foram caracterizados quanto a sua microdureza, número e profundidade das trincas. O regime de propagação durante os primeiros 50 ciclos foi controlado por mecanismo de fadiga de baixo ciclo, exibindo as maiores velocidade de propagação das trincas e o regime de propagação depois dos 50 ciclos foram controlados por mecanismos de fadiga de alto ciclo. A nucleação das trincas ocorreu predominantemente pela interface matriz/carboneto e pelo próprio carboneto, sendo a propagação das trincas predominantemente pela interconexão de carbonetos fraturados na superfície do material e predominantemente na interface matriz carboneto em camadas mais profundas do corpo de prova. Os resultados obtidos mostraram uma boa correlação entre o ensaio e o modelo numérico, permitindo uma maior confiabilidade para execução do modelo mecânico subsequente. Baseado nos resultados foi possível propor uma metodologia para a avaliação de ambos materiais submetidos a ciclos térmicos.
Titre en anglais
Study on the thermal cycling resistance of high chromium white cast iron and AISI D2 tool steel.
Mots-clés en anglais
AISI D2 tool steel
High chromium white cast iron
Thermal cycling
Resumé en anglais
This study presents an approach to evaluate the behavior of high chromium white cast iron and AISI D2 tool steel submitted at thermal cycles. It was developed a procedure for a thermal fatigue test in different times of cycles were done, using induced heating and water cooling. Due to the complexity of the phenomena involved, a FEM study was performed for solving the temperatures and superficial stresses fields. The control of superficial stress was done by changing the geometry of the test specimens, what was defined by computational simulation. The test specimens were evaluated the microstructure, microhardness and carbides contends before the test. After the test were evaluated microhardness, amount and depth of thermal fatigue cracks. The propagation during the earlier cycles was defined by mechanics of low cycle instead of after 100 cycles that was defined by mechanics of high cycle fatigue. This mechanics was observed by crack velocity analyses in both periods. The nucleation of thermal fatigue cracks initiate mostly at the matrix/carbide interface or at the carbide itself, being the cracks propagation was mainly by the interconnection of fractured carbides at surface and mainly at the interface matrix/carbide in the inner layer of the specimens test. The results obtained showed an adherence between the test and the numerical model, allowed a greater reliability to the subsequent mechanical model. Based on the results was possible propose a methodology for evaluation of both materials subjected a thermal cycles.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2012-04-09
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.