• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.3.2009.tde-19112010-093318
Document
Auteur
Nom complet
Eduardo Junca
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2009
Directeur
Jury
Tenório, Jorge Alberto Soares (Président)
Espinosa, Denise Crocce Romano
Sampaio, Carlos Hoffmann
Titre en portugais
Estudo da separação e aproveitamento da parte metálica e de óxidos presentes no resíduo gerado no corte de rochas ornamentais.
Mots-clés en portugais
Rochas ornamentais
Tratamento de resíduos sólidos
Resumé en portugais
Este trabalho tem como objetivo o estudo do reaproveitamento da parte metálica e a caracterização dos óxidos presente no resíduo de granito gerado na etapa de desdobramento. Inicialmente, foi feita a caracterização química e física do resíduo através de análise química, difração de raios-X, microscopia eletrônica de varredura e análise granulométrica. Após a caracterização do resíduo, foi dado inicio aos processos para a recuperação do Fe metálico que envolveram: separação magnética, mesa concentradora e ciclonagem. A separação magnética foi realizada em três etapas: a primeira onde se utilizou um separador magnético a úmido de alta intensidade, onde foi utilizado apenas o campo magnético remanescente do equipamento. Na segunda etapa, onde o material magnético obtido na primeira etapa foi submetido a uma nova separação magnética manual utilizando um imã de terras raras. Na terceira etapa, o material magnético obtido com o imã de terras raras foi submetido a uma separação magnética manual com um imã ferrítico. Nos ensaios de mesa concentradora, foram realizadas variações na inclinação da mesa, freqüência de oscilação e vazão de água de lavagem. Já nos ensaios de ciclone, o parâmetro variado foi à pressão de alimentação. Foram realizadas variações nos parâmetros dos equipamentos com o intuito de se aperfeiçoar e definir os melhores parâmetros para a recuperação do Fe metálico. Após cada ensaio, foi realizada a análise química volumétrica para a determinação do teor de Fe metálico obtido em cada produto. Pelos resultados obtidos, o método de separação magnética foi a que apresentou os melhores resultados, sendo possível a obtenção de um concentrado ferroso com 93% de Fe metálico e um concentrado granítico com 0,6% de Fe metálico. Já nos ensaios de mesa concentradora, o melhor resultado obtido foi um concentrado ferroso com apenas 13,7% de Fe metálico, e nos ensaios de ciclone foi possível à obtenção de um produto com apenas 7,2% de Fe metálico. A partir do concentrado ferroso e granítico obtido na separação magnética foi realizada a caracterização através de microscopia eletrônica de varredura, difração de raios-X e análise granulométrica. A partir do concentrado ferroso obtido, foram produzidos briquetes com uso de 2% de cal hidratada como aglomerante. Foram realizados testes de resistência mecânica a verde e a seco nos briquetes produzidos. Foi obtido uma resistência mecânica a verde de no máximo 1,02 kN e a seco de no máximo 3,59 kN.
Titre en anglais
Study of separation and reuse of metallic part and present oxides in residue generated in ornamental rocks cutting.
Mots-clés en anglais
Ornamental rocks
Solid waste management
Resumé en anglais
The aim of this work is to study the reuse of the metallic part and the characterization of oxides present in the waste from granite sawing. First, the chemical and physical characteristics of the waste were analyzed by chemical analysis, X-ray diffraction, scanning electron microscopy and size analysis. Procedures for the metallic iron recovery (magnetic separation, concentrator table, and cyclonic separation) were performed after the waste characterization. Magnetic separation was performed in three phases. First, using a high intensity wet magnetic separator, which only the remaining magnetic field of equipment was utilized. In the second phase, the magnetic material obtained in first phase was subjected to a new manual magnetic separation using rare earth magnets. In a third phase, magnetic material obtained with rare earth magnets was subjected to manual magnetic separation using ferrite magnets. In the experiments of concentrator table, were carried out changes in table inclination, oscillation frequency and wash water flow. For cyclone tests, the varied parameter was the water supply pressure. Variations in equipment parameters were performed in order to improve and decide the best parameters for recovery of metallic iron. After each experiment, volumetric chemical analysis was performed to determine the metallic iron content of each product. The results show that the magnetic separation method had the best results since it is possible to obtain a ferrous concentrated with 93.0 wt. % metallic iron and granite concentrated with 0.6 wt. % metallic iron. While for concentrator table tests, the best result presented a ferrous concentrated with only 13.6 wt. % metallic iron; and for cyclone tests, a product with only 7.2 wt. % of metallic iron was obtained. Ferrous and granite concentrated from magnetic separation were characterized by scanning electron microscopy, X-ray diffraction and size analysis. Using the obtained ferrous concentrated, briquettes were produced with 2 wt. % hydrated lime as binder. Produced briquettes were tested using dry and wet mechanical strength test. Wet mechanical strengths of up to 1.02kN were obtained, and a maximum of 3.59kN was registered to dry mechanical strength.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2010-12-15
 
AVERTISSEMENT: Le matériau se réfère à des documents provenant de cette thèse ou mémoire. Le contenu de ces documents est la responsabilité de l'auteur de la thèse ou mémoire.
  • Junca, Eduardo, et al. Briquetagem da granalha de aço recuperada do resíduo de rochas ornamentais. REM. Revista Escola de Minas , 2011, vol. 64, p. 175-179.
  • Junca, E., et al. Caracterização da granalha de aço recuperada do resíduo de rochas ornamentais por separação magnética. In Congresso Brasileiro de Engenharia e Ciência dos Materiais, Campos do Jordão, 2010. Congresso Brasileiro de Engenharia e Ciência dos Materiais., 2010.
  • Junca, E., et al. Caracterização dos óxidos e do metal obtidos a partir de resíduo gerado no corte de granito. In 18º Cbecimat Congresso Brasileiro de Ciência e Engenharia de Materiais, Recife, 2008. 18º Cbecimat Congresso Brasileiro de Ciência e Engenharia de Materiais., 2008.
  • JUNCA, E., et al. Estudo da separação magnética e ciclonagem na recuperação do FE metálico presente no resíduo de granito. In 65º Congresso da ABM, Rio de Janeiro, 2010. 65º Congresso da ABM.São Paulo : ABM, 2010.
  • JUNCA, E., et al. Estudo da viabilidade técnica da utilização do metal contido nos resíduos de rochas ornamentais nos processos de fabricação de aço. In 40º Seminário de Aciaria, São Paulo, 2009. Anais.São Paulo : ABM, 2009.
  • Junca, E., et al. RECUPERAÇÃO DA PARTE METÁLICA CONTIDA EM RESÍDUOS DE ROCHAS ORNAMENTAIS. In Congresso da ABM, Belo Horizonte, 2009. 64º Congresso da ABM.SãoPaulo : ABM, 2009.
  • JUNCA, E., et al. Resíduo do corte de granito: novas rotas para a destinação final. In 66º Congresso da ABM, São Paulo, 2011. 66º Congresso da ABM.São Paulo : ABM, 2011.
  • RODRIGUES, G. F., et al. Estudo da incorporação de resíduos do corte de mármores e granitos em matéria-prima para a fabricação de lã de vidro. In 65º Congresso da ABM, Rio de Janeiro, 2010. 65º Congresso da ABM.São Paulo : ABM, 2010.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.