Tesis Doctoral
DOI
https://doi.org/10.11606/T.3.2006.tde-19042007-155843
Documento
Autor
Nombre completo
Guillermo Palmer Martín
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2006
Director
Tribunal
Demarquette, Nicole Raymonde (Presidente)
Canevarolo Júnior, Sebastião Vicente
Giudici, Reinaldo
Hernández López, José Ignacio
Petri, Denise Freitas Siqueira
Título en portugués
Estudo da viscoelasticidade linear e não linear de misturas de PP/PA-6 compatibilizadas ou não.
Palabras clave en portugués
Fluxo elongacional
Misturas poliméricas
PP/PA-6
Retração de fibra e fibra quebrante
Tensão interfacial
Viscoelasticidade linear
Viscoelasticidade não linear
Resumen en portugués
Neste trabalho estudou-se o comportamento reológico e morfológico da mistura polimérica imiscível de polipropileno e poliamida. Como resultado deste estudo obtiveram-se valores de tensão interfacial entre 10mN/m e 13mN/m. A tensão interfacial diminuiu em até 87% quando a mistura é compatibilizada com polipropileno maleado. A análise morfológica no regime de viscoelasticidade linear quando avaliada uma morfologia de emulsão de poliamida em polipropileno revelou diâmetro médio da fase dispersa entre 1,5µm e 20µm. O diâmetro das gotas da fase dispersa diminuiu com a adição de polipropileno maleado chegando a reduções de até 98%, mantendo-se constante a concentração da fase dispersa. No regime de viscoelasticidade não linear foram testados modelos para avaliar o comportamento da mistura em fluxos de cisalhamento e extensão, sendo que somente para os fluxos de extensão foi obtida boa correlação dos resultados experimentais com as previsões teóricas.
Título en inglés
Study of lineal and non lineal viscoelastic behavior of PP/PA-6 polymer blends compatibilized or no.
Palabras clave en inglés
Extensional flow
Fiber retraction and breaking thread
Interfacial tension
Lineal viscoelastic
Non lineal viscoelastic
Polymer blends
PP/PA-6
Resumen en inglés
Rheological and morphological behaviour of polypropylene and polyamide polymer blend was studied. The values of interfacial tension were obtained between 10mN/m and 13mN/m. The interfacial tension decreased in 87% for compatibilized blend. Morphology analysis for linear viscoelastic regime shows dispersed drop diameter between 1,5µm and 20µm. The diameter of the drops decreased with the addition of maleic polypropylene reducing until 98%, keeping constant the concentration of the disperse phase. In non linear viscoelastic regime different models were tested to evaluate the behavior of the blends in shear and elongacional flows. However, only the elongacional flow results were acquired with theoretical - experimental corroboration.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-08-25
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.