• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Dissertação de Mestrado
DOI
10.11606/D.3.2014.tde-19032015-154341
Documento
Autor
Nome completo
Aurianny Pereira Lima
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2014
Orientador
Banca examinadora
Hui, Wang Shu (Presidente)
Carastan, Danilo Justino
Drumond, Walker Soares
Título em português
Estudo da fase cristalina beta em compósitos de polipropileno.
Palavras-chave em português
Materiais compósitos poliméricos
Resumo em português
O presente trabalho busca o entendimento do aparecimento da fase cristalina em compósitos de polipropileno isotático, que contém carbonato de cálcio, em presença ou não de polipropileno modificado com anidrido maléico (PPMA). Vários tipos de CaCO3 foram utilizados: com diâmetros médios de 0,9 m, com e sem tratamento superficial, 2,5 m e 3,0 m. As duas séries de compósitos, com e sem PPMA, denominadas iPP/CaCO3/PPMA e iPP/CaCO3, foram formuladas com as seguintes razões mássicas, 94,5/5/0,5% e 95/5, respectivamente. Em ambas as séries, observou-se a ocorrência das fases cristalinas e do polipropileno; entretanto, a concentração relativa variou de acordo com o tipo de compósito. A caracterização das fases cristalinas presentes nos compósitos foi realizada utilizando a difratometria de raio-x (DRX) e análises térmicas, principalmente, calorimetria diferencial exploratória (DSC). As análises por DSC incluíram o estudo cinético da cristalização isotérmica e não isotérmica dos compósitos. Os resultados obtidos permitiram identificar os compósitos com maior concentração de fase cristalina e relacionar a sua formação com os constituintes presentes nos compósitos.
Título em inglês
Study of beta crystalline phase in polypropylene composites.
Palavras-chave em inglês
Composite materials polymeric
Resumo em inglês
The present work aims to understand the occurrence of the beta crystalline phase in composites of isotactic polypropylene with calcium carbonate in the presence or not of polypropylene grafted maleic anhydride (PPMA). CaCO3 having different average diameter were used: 0.9 m with and without surface treatment, 2.5 m and 3.0 m. Both series of composites, one with PPMA and another without, named iPP/CaCO3/PPMA and iPP/CaCO3, were formulated at the following mass proportions: 94.5/5/0.5% and 95/5, respectively. The presence of the e crystalline phases in polypropylene were observed. However, the relative concentration of such phases depended on the composite composition. The characterization of the crystalline phases in composites were performed by using x-ray diffraction (DRX) and thermal analyses, mainly, differential scanning calorimetry (DSC). DSC analysis was used to investigate isothermal crystallization kinetic and nonisothermal crystallization kinetic. The results allowed the identification of the composites with higher concentration of crystalline phase and it was possible to attribute the phase occurrence to the presence of specific constituents of the composites.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2015-03-24
 
AVISO: O material descrito abaixo refere-se a trabalhos decorrentes desta tese ou dissertação. O conteúdo desses trabalhos é de inteira responsabilidade do autor da tese ou dissertação.
  • LIMA, A. P., SAKAHARA, R. M., e Wang, Shu Hui. Análise da ocorrência de fase cristalina beta em compósitos de polipropileno isotático, carbonato de cálcio com e sem polipropileno modificado com anidrido maléico. In 12º Congresso Brasileiro de Polímeros, Florianópolis, 2013. Anais do 12º Congresso Brasileiro de Polímeros.São Carlos : ABPOL, 2013.
  • WANG, S. H., et al. Fluoração por plasma da superfície de filmes de poliuretano para aplicações médicas. In 6ºCBPOL - IX International Macromolecular Colloquium, Gramado. nais do 6ºCBPOL - IX International Macromolecular Colloquium.Sao Carlos : ABPOL, 2001.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.