• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
10.11606/D.3.2014.tde-19032015-154341
Documento
Autor
Nombre completo
Aurianny Pereira Lima
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2014
Director
Tribunal
Hui, Wang Shu (Presidente)
Carastan, Danilo Justino
Drumond, Walker Soares
Título en portugués
Estudo da fase cristalina beta em compósitos de polipropileno.
Palabras clave en portugués
Materiais compósitos poliméricos
Resumen en portugués
O presente trabalho busca o entendimento do aparecimento da fase cristalina em compósitos de polipropileno isotático, que contém carbonato de cálcio, em presença ou não de polipropileno modificado com anidrido maléico (PPMA). Vários tipos de CaCO3 foram utilizados: com diâmetros médios de 0,9 m, com e sem tratamento superficial, 2,5 m e 3,0 m. As duas séries de compósitos, com e sem PPMA, denominadas iPP/CaCO3/PPMA e iPP/CaCO3, foram formuladas com as seguintes razões mássicas, 94,5/5/0,5% e 95/5, respectivamente. Em ambas as séries, observou-se a ocorrência das fases cristalinas e do polipropileno; entretanto, a concentração relativa variou de acordo com o tipo de compósito. A caracterização das fases cristalinas presentes nos compósitos foi realizada utilizando a difratometria de raio-x (DRX) e análises térmicas, principalmente, calorimetria diferencial exploratória (DSC). As análises por DSC incluíram o estudo cinético da cristalização isotérmica e não isotérmica dos compósitos. Os resultados obtidos permitiram identificar os compósitos com maior concentração de fase cristalina e relacionar a sua formação com os constituintes presentes nos compósitos.
Título en inglés
Study of beta crystalline phase in polypropylene composites.
Palabras clave en inglés
Composite materials polymeric
Resumen en inglés
The present work aims to understand the occurrence of the beta crystalline phase in composites of isotactic polypropylene with calcium carbonate in the presence or not of polypropylene grafted maleic anhydride (PPMA). CaCO3 having different average diameter were used: 0.9 m with and without surface treatment, 2.5 m and 3.0 m. Both series of composites, one with PPMA and another without, named iPP/CaCO3/PPMA and iPP/CaCO3, were formulated at the following mass proportions: 94.5/5/0.5% and 95/5, respectively. The presence of the e crystalline phases in polypropylene were observed. However, the relative concentration of such phases depended on the composite composition. The characterization of the crystalline phases in composites were performed by using x-ray diffraction (DRX) and thermal analyses, mainly, differential scanning calorimetry (DSC). DSC analysis was used to investigate isothermal crystallization kinetic and nonisothermal crystallization kinetic. The results allowed the identification of the composites with higher concentration of crystalline phase and it was possible to attribute the phase occurrence to the presence of specific constituents of the composites.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-03-24
 
ADVERTENCIA: El material descrito abajo se refiere a los trabajos derivados de esta tesis o disertación. El contenido de estos documentos es responsabilidad del autor de la tesis o disertación.
  • LIMA, A. P., SAKAHARA, R. M., e Wang, Shu Hui. Análise da ocorrência de fase cristalina beta em compósitos de polipropileno isotático, carbonato de cálcio com e sem polipropileno modificado com anidrido maléico. In 12º Congresso Brasileiro de Polímeros, Florianópolis, 2013. Anais do 12º Congresso Brasileiro de Polímeros.São Carlos : ABPOL, 2013.
  • WANG, S. H., et al. Fluoração por plasma da superfície de filmes de poliuretano para aplicações médicas. In 6ºCBPOL - IX International Macromolecular Colloquium, Gramado. nais do 6ºCBPOL - IX International Macromolecular Colloquium.Sao Carlos : ABPOL, 2001.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2018. Todos los derechos reservados.