Mémoire de Maîtrise
DOI
10.11606/D.3.2013.tde-16122014-161458
Document
Auteur
Nom complet
Adriana Maria Sanchez Gonzalez
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2013
Directeur
Jury
Valera, Ticiane Sanches (Président)
Akerman, Mauro
Vieira Coelho, Antonio Carlos
Titre en portugais
Cristalização de um vidro de basalto.
Mots-clés en portugais
Agente de nucleação
Basalto
Cristalização
Tratamento térmico
Resumé en portugais
Os materiais vitrocerâmicos de basalto representam uma importante família de vitrocerâmicos. Sendo que um dos desempenhos técnicos exigidos atualmente é o efeito anti-desgaste dos materiais, as vitrocerâmicas de basalto cobrem essa necessidade e têm uma aplicação direta por suas boas propriedades mecânicas e anti-abrasivas, além da vantagem que têm as rochas basálticas quanto à baixa temperatura de fusão e maior fluidez do fundido, o que as torna mais adequadas para o processamento cerâmico. No presente trabalho, rejeitos da mineração de rocha basáltica da região de Campinas, São Paulo, foram fundidos em escala laboratorial em forno elétrico a 1350°C, usando cadinhos de alta alumina, para a obtenção de uma primeira série de amostras de vidro. Mais uma série foi obtida, realizando a fusão da matéria-prima com adição de 0,5% em massa de Cr2O3 como agente de nucleação. Os vidros foram tratados termicamente à máxima temperatura de cristalização como sendo 880°C e 820°C durante 5, 10, 20, 30 e 60 minutos e 5, 20 e 60 minutos respectivamente. A evolução das fases cristalinas foi acompanhada por análise de densidade (método de Arquimedes) e difração de raios X (DRX). Foi realizada a medição da microdureza Vickers e resistência à micro-abrasão, e o vidro cristalizado observou-se por microscopia eletrônica de varredura (MEV). Os vidros da primeira série foram também moídos, até tamanhos de partícula ASTM 80 e ASTM 325, para avaliar sua capacidade de cristalização como pó de vidro. Eles foram caracterizados mediante DRX e MEV.
Titre en anglais
Crystallization of a basalt glass.
Mots-clés en anglais
Basalt
Crystallization
Heat treatment
Nucleating agent
Resumé en anglais
Basalt glass-ceramics represent one of the most important family of glass-ceramics. The wear resistant, is now the technical performance requirement in material, basalt glass-ceramics cover that need and have a direct application for their good mechanical and anti-abrasive properties. In addition, the basaltic rocks have the advantage of a low melt temperature and higher fluidity melt. In this paper, a mining waste of basaltic rock from the city of Campinas, São Paulo, was melted in laboratory scale, in an electric furnace at 1350°C, in high-alumina crucibles, to obtain the first series of basalt glass samples. Other series was obtained by melting of the raw material with addition of 0,5% wt. of Cr2O3 as a nucleating agent. The glasses were heat treated at the maximum crystallization temperature: 880oC during 5, 10, 20, 30, and 60 minutes and 820°C during 5, 20 and 60 minutes, respectively. The evolution of the crystalline phases was accompanied by density and X-ray diffraction (XRD) analyses. Vickers hardness and micro-abrasion resistance of the samples were also carried out, and the crystallized glasses were observed in a scanning electron microscope (SEM). The first series of glasses were also milled, until particle sizes ASTM 80 e ASTM 325, for the evaluation of their ability to crystallization as glass powder. They were characterized by XRD and SEM.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2015-01-12
 
AVERTISSEMENT: Le matériau se réfère à des documents provenant de cette thèse ou mémoire. Le contenu de ces documents est la responsabilité de l'auteur de la thèse ou mémoire.
  • GONZALEZ, A. S., VALERA, T. S., e TOFFOLI, SAMUEL M. Design of a ceramic splip for electrical porcelain insulators, using clay dispersed in a ball mill. Materials Science Forum , 2013.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.