Master's Dissertation
DOI
10.11606/D.3.2013.tde-16122014-161458
Document
Author
Full name
Adriana Maria Sanchez Gonzalez
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2013
Supervisor
Committee
Valera, Ticiane Sanches (President)
Akerman, Mauro
Vieira Coelho, Antonio Carlos
Title in Portuguese
Cristalização de um vidro de basalto.
Keywords in Portuguese
Agente de nucleação
Basalto
Cristalização
Tratamento térmico
Abstract in Portuguese
Os materiais vitrocerâmicos de basalto representam uma importante família de vitrocerâmicos. Sendo que um dos desempenhos técnicos exigidos atualmente é o efeito anti-desgaste dos materiais, as vitrocerâmicas de basalto cobrem essa necessidade e têm uma aplicação direta por suas boas propriedades mecânicas e anti-abrasivas, além da vantagem que têm as rochas basálticas quanto à baixa temperatura de fusão e maior fluidez do fundido, o que as torna mais adequadas para o processamento cerâmico. No presente trabalho, rejeitos da mineração de rocha basáltica da região de Campinas, São Paulo, foram fundidos em escala laboratorial em forno elétrico a 1350°C, usando cadinhos de alta alumina, para a obtenção de uma primeira série de amostras de vidro. Mais uma série foi obtida, realizando a fusão da matéria-prima com adição de 0,5% em massa de Cr2O3 como agente de nucleação. Os vidros foram tratados termicamente à máxima temperatura de cristalização como sendo 880°C e 820°C durante 5, 10, 20, 30 e 60 minutos e 5, 20 e 60 minutos respectivamente. A evolução das fases cristalinas foi acompanhada por análise de densidade (método de Arquimedes) e difração de raios X (DRX). Foi realizada a medição da microdureza Vickers e resistência à micro-abrasão, e o vidro cristalizado observou-se por microscopia eletrônica de varredura (MEV). Os vidros da primeira série foram também moídos, até tamanhos de partícula ASTM 80 e ASTM 325, para avaliar sua capacidade de cristalização como pó de vidro. Eles foram caracterizados mediante DRX e MEV.
Title in English
Crystallization of a basalt glass.
Keywords in English
Basalt
Crystallization
Heat treatment
Nucleating agent
Abstract in English
Basalt glass-ceramics represent one of the most important family of glass-ceramics. The wear resistant, is now the technical performance requirement in material, basalt glass-ceramics cover that need and have a direct application for their good mechanical and anti-abrasive properties. In addition, the basaltic rocks have the advantage of a low melt temperature and higher fluidity melt. In this paper, a mining waste of basaltic rock from the city of Campinas, São Paulo, was melted in laboratory scale, in an electric furnace at 1350°C, in high-alumina crucibles, to obtain the first series of basalt glass samples. Other series was obtained by melting of the raw material with addition of 0,5% wt. of Cr2O3 as a nucleating agent. The glasses were heat treated at the maximum crystallization temperature: 880oC during 5, 10, 20, 30, and 60 minutes and 820°C during 5, 20 and 60 minutes, respectively. The evolution of the crystalline phases was accompanied by density and X-ray diffraction (XRD) analyses. Vickers hardness and micro-abrasion resistance of the samples were also carried out, and the crystallized glasses were observed in a scanning electron microscope (SEM). The first series of glasses were also milled, until particle sizes ASTM 80 e ASTM 325, for the evaluation of their ability to crystallization as glass powder. They were characterized by XRD and SEM.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2015-01-12
 
WARNING: The material described below relates to works resulting from this thesis or dissertation. The contents of these works are the author's responsibility.
  • GONZALEZ, A. S., VALERA, T. S., e TOFFOLI, SAMUEL M. Design of a ceramic splip for electrical porcelain insulators, using clay dispersed in a ball mill. Materials Science Forum , 2013.