Dissertação de Mestrado
DOI
10.11606/D.3.2015.tde-16112015-002331
Documento
Autor
Nome completo
Anderson Clayton Nascimento Ribeiro
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2015
Orientador
Banca examinadora
Brandi, Sergio Duarte (Presidente)
Ramalho, José Pinto
Schön, Claudio Geraldo
Título em português
Avaliação da soldagem do aço naval AH36 microligado soldado pelo processo arco submerso com um e dois arames.
Palavras-chave em português
Aços microligados
Soldagem a arco
Resumo em português
Diversas pesquisas em processos de soldagem para construção naval concentram-se em reduzir peso, aumentar a eficiência de energia, melhorar a resistência à corrosão e à tenacidade, bem como reduzir custos e tempo na construção dos navios. O aço naval microligado, AH36, apresenta boa correlação entre estrutura, propriedades mecânicas e soldabilidade. Estas características se devem principalmente a redução dos teores de carbono em função do uso de elementos microligantes como V, Nb e Ti, e do tipo de processo de obtenção das chapas pelo processo termomecânico seguido de resfriamento acelerado (em inglês: Thermomechanical control process -TMCP). Assim, o objetivo deste trabalho é avaliar a soldagem do aço naval AH 36 pelo processo de arco submerso com um e dois arames. Para tanto foram empregados os ensaios mecânicos de tração, de dobramento e de dureza. A tenacidade foi determinada pelo ensaio de Charpy com entalhe em V. Para caracterização metalográfica foram aplicadas as seguintes técnicas: Microscopia óptica (MO) e Microscopia eletrônica de varredura (MEV) e difração de raios X. Os resultados mostraram que as juntas soldadas apresentaram limite de resistência máxima de 561 MPa, com rompimento localizado no metal de base. No ensaio de microdureza foi observado que a região de crescimento de grão da zona afetada pelo calor, no experimento com a técnica Tandem, apresentou-se a região mais rígida das juntas analisadas, também o valor de microdureza no metal de solda foi 10% maior que no metal de base. Os resultados dos ensaios de impacto Charpy V mostraram que a temperatura de transição dúctil frágil do metal de base é de -30ºC. Da mesma maneira, o menor valor de energia absorvida foi para região do metal de solda. Através da análise da micrografia foi possível identificar diferentes morfologias de ferrita, a presença de perlita e pequenas regiões de martensita, bem como a presença de agregados MA.
Título em inglês
Evaluate the welding microalloyed steel AH36 by submerged arc process with one and two wires.
Palavras-chave em inglês
Arc welding
Microalloyed steel
Resumo em inglês
Several researches in welding processes for shipbuilding has been focusing on reducing weight, increasing energy efficiency, improving corrosion resistance and toughness as well as reducing costs and time in the construction of ships. The microalloyed steel AH36 shipbuilding presents a good correlation among structure, mechanical properties and weldability. These features are mainly because reduction in carbon content due to the use of microalloying elements such as V, Nb and Ti, together with the process of steel plates by thermomechanical control process (TMCP), Therefore, the objective of this study is to evaluate the welding of shipbuilding steel AH 36 by submerged arc process with one and two wires. It was utilized tests such as: tensile, bending and hardness tests. The toughness was determined by Charpy V-Notch test. The metallographic characterization was carried out by the following techniques: optical microscopy (OM) and scanning electron microscopy (SEM) and X-Rays diffraction. The results showed that the tensile test for welded joints presented maximum resistance limit of 561 MPa, and the rupture was located in the base metal. Microhardness test showed that the region of coarse grain of heat affected zone, in the tandem submerged arc welding (SAW), presented the hardest region of the welded joint, also the microhardness value in the weld metal was 10% greater than the metal base. Charpy V notch test tests depicted a ductile brittle transition temperature at about -30 ºC. In the same way, the lowest absorbed energy was identified in the weld metal region. Through microstructure characterization it was possible to identify different morphologies of ferrite, pearlite and the small presence of martensite, as well as, the presence of aggregates MA.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Dissertacao_acnr.pdf (10.82 Mbytes)
Data de Publicação
2015-11-25
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.