Tese de Doutorado
DOI
10.11606/T.3.2013.tde-15082014-151305
Documento
Autor
Nome completo
Litzy Lina Choquechambi Catorceno
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2013
Orientador
Banca examinadora
Padilha, Angelo Fernando (Presidente)
Lima, Nelson Batista de
Martorano, Marcelo de Aquino
Melo, Mirian de Lourdes Noronha Motta
Rios, Paulo Rangel
Título em português
Estudo do encruamento, recristalização e crescimento de grão em chapa da liga de magnésio AZ31B (Mg - 3%Al - 1%Zn - 0,3%Mn).
Palavras-chave em português
Caracterização microestrutural
Liga de magnésio
Recristalização
Textura
Resumo em português
As ligas de magnésio atraíram a atenção novamente nos últimos anos por causa de suas propriedades de baixa densidade, resistência à tração e rigidez específica. Por outro lado, a maior limitação para o uso de ligas trabalhadas é a baixa conformabilidade em temperatura ambiente devido à estrutura hexagonal compacta (HCP) das ligas. O presente trabalho de pesquisa teve como objetivo estudar o encruamento, recristalização e crescimento de grãos durante a laminação de liga magnésio AZ31B em alta e baixa temperatura, analisando a evolução da microestrutura, da textura e a variação das propriedades sensíveis à microestrutura. A liga AZ31B é sensível à taxa de deformação em alta temperatura, entretanto, a anisotropia é negativamente afetada na laminação a frio, portanto, apresenta uma melhor laminação na faixa de temperaturas de 200 a 300ºC, devido ao refinamento de grãos, causado pela recuperação e recristalização dinâmica. O estudo foi realizado em amostras de uma chapa de liga de magnésio AZ31B recristalizada (2 mm de espessura). Amostras foram deformadas por laminação em temperaturas diferentes (25, 100, 200, 250 e 300ºC) e com diferentes taxas de deformação. A caracterização microestrutural foi realizada com auxílio de várias técnicas complementares de análise microestrutural, tais como microscopia óptica, microscopia eletrônica de varredura, análise de raios-X por dispersão de energia, difração de raios X e microdureza Vickers. A deformabilidade e a ocorrência de recristalização dinâmica e crescimento de grãos mostraram forte dependência com as condições de laminação. Na laminação a frio, o refinamento de grão foi mais efetivo com baixas taxas de deformação (1,6 s-1) do que na laminação a quente. Entretanto, a intensa textura basal foi enfraquecida em temperaturas próximas a 300ºC e com taxas de deformação próximas a 3,5 s-1. A ductilidade das ligas pode ser melhorada em altas temperaturas de deformação, pelo refinamento dos grãos que produz a diminuição da fração volumétrica das regiões macladas e pelo aumento do número de sistemas de deslizamento, além do enfraquecimento da intensa textura basal, característica das ligas de magnésio.
Título em inglês
Study of strain hardening, recrystallization and grain growth in AZ31B magnesium alloy sheet.
Palavras-chave em inglês
Magnesium alloy
Microstructural characterization
Recrystallization
Texture
Resumo em inglês
Magnesium alloys have attracted the attention again in recent years because of their low density, their specific tensile strength and rigidity. However, the greatest limitation for the usage of wrought magnesium alloys is their poor formability at room temperature due to the hexagonal closed packed (HCP) crystal structure. The present research focused on study the work-hardening, recrystallization and grain growth during rolling of AZ31B magnesium alloy at low and high rolling temperature. It was made through the analysis of microstructure and texture evolution and variations of microstructure-sensitive properties. The AZ31 magnesium alloy is sensitive to strain rate at high temperature, meanwhile, the anisotropy is adversely impacted in cold rolling sheets. Thus, AZ31B magnesium alloy exhibits better workability in 200-300°C temperature range due to the grain refinement caused by dynamic recovery and dynamic recrystallization. This research was carried out on samples of recrystallized sheet (2 mm in thickness). Samples were deformed by rolling at different temperatures (25, 100, 200, 250 and 300°C), using different strain rates. Microstructural characterization was done by using several complementary techniques of microstructural analysis, such as optical microscopy, scanning electron microscopy, X-ray analysis by energy dispersive, X-ray diffraction and Vickers microhardness tests. A competition between dynamic recrystallization and grain growth depends on rolling conditions. Low strain rate (1,6 s-1) at cold rolling improved more effective in refining grains than warm rolling. Meanwhile, the intense basal texture was weakened at 300°C with a high strain rate of 3,5 s-1. The ductility of magnesium alloys can be greatly improved at high temperature, with a fine grain structure that causes the reduced volume fraction of twins, and an increase the number of slip systems, weakening the intense basal texture, rather characteristic for magnesium alloys.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
tese_Litzy.pdf (12.77 Mbytes)
Data de Publicação
2015-01-08
 
AVISO: O material descrito abaixo refere-se a trabalhos decorrentes desta tese ou dissertação. O conteúdo desses trabalhos é de inteira responsabilidade do autor da tese ou dissertação.
  • CATORCENO, L. L. C., and PADILHA, A. F. Effect of rolling temperature on the AZ31B magnesium alloy microstructure. In TMS 2012 Annual Meeting & Exhibition, Orlando, USA, 2012. Magnesium Technology 2012. : TMS, 2012.