Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.3.2012.tde-13062013-123100
Document
Auteur
Nom complet
Rafael Eiji Toma
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2012
Directeur
Jury
Brandi, Sérgio Duarte (Président)
Carreira Neto, Manoel
Schön, Cláudio Geraldo
Titre en portugais
Comparação de juntas soldadas de aço inoxidável AISI 304 para aplicação em baixa temperatura utilizando-se a soldagem por arco submerso.
Mots-clés en portugais
Aço inoxidável AISI 304
Baixa temperatura
Soldagem por arco submerso
Resumé en portugais
Aços inoxidáveis austeníticos são indicados para aplicações a baixas temperaturas por praticamente não apresentarem temperatura de transição dúctil/frágil. Quando estes aços são soldados há a formação de ferrita na zona fundida que, dependendo da morfologia e da quantidade, pode induzir uma temperatura de transição dúctil/frágil. Este trabalho busca estudar as propriedades mecânicas e microestruturais a baixas temperaturas (-100°C) na zona fundida do cordão de solda. Chapas de aço inoxidável AISI 304 com 25,4 mm de espessura foram soldadas pelo processo de soldagem a arco submerso, empregando-se um arame ER 308L, e dois tipos de fluxos distintos: um neutro e um auto-compensante em cromo. Os procedimentos de soldagem foram realizados utilizando-se corrente contínua em polaridade reversa e corrente alternada de onda quadrada. Esta apresentou melhores resultados de tenacidade que a soldagem em corrente contínua para os dois fluxos estudados. Os corpos de prova soldados com fluxo neutro apresentaram maior tenacidade que os soldados com fluxo autocompensante em cromo, comparando-se o mesmo tipo de corrente na soldagem.
Titre en anglais
Comparison of AISI 304 stainless steel weld joints for low temperature application using submerged arc welding.
Mots-clés en anglais
AISI 304 stainless steel
Low temperature
Submerged arc welding
Resumé en anglais
Austenitic stainless steels are recommended for low temperature applications due to a very low ductile/brittle transition. When this stainless steel type is welded, there is formation of delta ferrite in the fusion zone which, depending on its morphology and distribution may increase ductile/brittle temperature transition to higher values compared with base metal. This work aims at studying the mechanical properties and microstructure at low temperatures (-100°C) on the weld bead fusion zone using AISI 304 plates 1 inch thick which were welded with submerged arc welding process using ER308L and two different fluxes types: a neutral and a chromium auto-compensating one. The welding procedures were made using reverse polarity continuous current and square wave alternate current. The latter presented better toughness results than the continuous current for both fluxes types. The neutral flux led to greater toughness than the chromium auto-compensating flux, comparing the same current type output.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2013-06-26
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.