Master's Dissertation
DOI
https://doi.org/10.11606/D.3.2010.tde-12082010-172944
Document
Author
Full name
Heber Pires Otomar
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2010
Supervisor
Committee
Plaut, Ronald Lesley (President)
Lima, Nelson Batista de
Padilha, Angelo Fernando
Title in Portuguese
Estudo comparativo da estampabilidade da liga de aluminio AA1050 partindo de placas obtidas por vazamento direto e bobinas obtidas por vazamento contínuo.
Keywords in Portuguese
Alumínio
Conformação mecânica
Curva limite de conformação
Liga AA1050
Textura
Abstract in Portuguese
A estampabilidade das ligas de alumínio é um assunto que interessa à vários segmentos industriais, pois é largamente aplicada na fabricação de peças e componentes. Entre dois processos de solidificação do alumínio, a solidificação de placa (DC) e o vazamento contínuo via caster (CC), o processo caster apresenta um histórico de condições inferiores para estampagens mais críticas nestas ligas. Este estudo visa avaliar as diferenças entre os processos de fabricação para chapas na liga AA1050 laminadas para 1,80mm, na condição recristalizada, durante a laminação e tratamento térmico e, caracterizar a microestrutura e textura. Ensaios de conformabilidade foram utilizados para identificar qual processo apresenta o melhor desempenho para estampagem. Para realização do estudo foram analisados três lotes de produção da Companhia Brasileira de Alumínio CBA, proveniente de processo de vazamento tipo placa (DC), e dois outros lotes provenientes de processo de vazamento tipo caster (CC) sendo, um com homogeneização intermediária e outro sem homogeneização. Os materiais foram processados em laminadores e fornos de escala industrial. A estrutura metalúrgica foi caracterizada através de ensaios metalográficos ao longo dos processos, obtendo-se a distribuição de intermetálicos e a estrutura cristalina através de microscopia ótica. A microscopia eletrônica também foi empregada para identificação dos precipitados. Ensaio de tração foi utilizado para identificar a variação das propriedades mecânicas ao longo do processo. Na condição final, ou seja, após laminação para 1,80mm de espessura com posterior recozimento foram utilizados os ensaios de orelhamento (earing), Erichsen, análise da anisotropia e levantamento da curva limite de conformação (CLC), para identificar qual processo apresenta o melhor resultado de conformação. A fim de entender as mudanças ocorridas nos materiais, foi estudada a macrotextura gerada no material ao longo da espessura da chapa. Na condição final foi realizada a microtextura no processo placa e caster sem homogeneização. A microestrutura dos materiais apresentou resultados distintos entre os processos, o material de placa mais homogêneo, tanto na distribuição dos intermetálicos quanto na estrutura granular. As propriedades mecânicas do caster, (LRT, LE e Dureza) ficaram um pouco superiores às do material de placa. O ensaio de Erichsen indicou que o material de placa resistiu a uma maior profundidade de conformação. No ensaio de orelhamento o caster sem homogeneização apresentou o menor índice, porém o material de placa apresentou a maior profundidade de conformação. As texturas encontradas ao longo dos processos foram principalmente a tipo Goss <100>, Cubo <001> e Cubo rodado <110>. Também foram identificadas texturas típicas de cisalhamento após a laminação a frio, Dillamore {4 4 11} <11 11 > e Taylor {11 11 8}<4 4 >. A textura tipo S~<634> que é favorável a conformabilidade de metais CFC, apareceu ao final dos processos. Na curva limite de conformação (CLC) foi possível identificar que o caster com homogeneização apresentou o melhor resultado que os outros dois processos. Os ensaios de conformabilidade indicaram que o material de placa tem uma estampagem mais profunda, enquanto que o material de caster sem homogeneização tem um orelhamento menor.
Title in English
Comparative study of the deep drawing alloy AA1050 from plates obtained by direct casting and coils obtained by continuos casting.
Keywords in English
Alloy AA1050
Aluminum
Forming limit diagram
Mechanical working
Texture
Abstract in English
Stampability of aluminum alloys is a subject of interest to several industrial sectors because they are largely used in the fabrication of several parts and components. The choice is based upon the stampability and the relative manufacturing capability in relation to other aluminum alloys that contain larger amounts of alloying elements and, consequently, higher mechanical properties. When comparing two solidification processes, namely the direct chill (DC) and the continuous casting (CC) via caster, the CC process historically presents inferior performance for the more critical stampings in these alloys. This study aims at the evaluation of the differences between the fabrication processes (routes) of AA1050 rolled to 1,80mm sheets in the conditions as annealed, rolled and after heat treatment and to characterize their microstructure and texture. Stamping tests have been performed to identify which process presents best stamping performance. To carry out these studies three production lots from the Companhia Brasileira de Alumínio CBA have been employed namely one from the DC method and two other lots from the DC method, one with and one without an intermediate homogenization treatment. All materials have been processed in rolling mills and ovens in an industrial scale. The metallurgical structure has been characterized by optical and electronic microscopy throughout the processes analyzing the intermetallics and precipitate distribution. Tensile tests have been perfumed to identify the evolution of the mechanical properties throughout the process. In the final condition, i.e., after rolling down to 1,80mm and annealing, earing tests, Erichsen drawing tests and anisotropy have been evaluated together with the Forming Limit Diagram( FLD), to evaluate which process presented the best results in terms of formability. In order to understand the changes that occurred, the macrotexture has been studied along the thickness of the rolled sheets. In the final condition, the microtexture of the DC and the CC without homogenization have been compared. Different microstructures have been obtained for the studied processes: the DC material was more homogeneous, both in terms of intemetallic distribution and grain size. The mechanical properties of the CC material, in terms of TS, YS and hardness, were sligthly higher than those for the DC material. Erichsen test showed that the DC material takes higher deformations. Earing tests showed that the CC material without homogeneization presented the best results however the DC material presented better cup height. The textures analyzed for the different process stages were mainly of the Goss <100>, Cube <001> and rotated Cube <110> types. Also some typical shear textures of the Dillamore {4 4 11} <11 11 > and Taylor {11 11 8} <4 4 > types have been observed in cold rolled sheets. The S~<634> type, which is favourable for the formability of FCC metals, showed up in the final processing stages. The FLD showed that the CC with homogenization presented better results when compared to the other two processing routes. The stamping tests showed that the DC material presents higher drawability while the CC material without homogenization presents lower earing index.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2010-09-15
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2024. All rights reserved.