Tese de Doutorado
DOI
10.11606/T.3.2016.tde-10112016-101541
Documento
Autor
Nome completo
João de Araújo Junior
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2014
Orientador
Banca examinadora
Wiebeck, Hélio (Presidente)
Mercuri, Lucildes Pita
Esper, Fábio José
Hui, Wang Shu
Valera, Ticiane Sanches
Título em português
Estudo da degradação parcial de filmes de blendas de poli(tereftalato de butileno-co-adipato de butileno) e poli(ácido láctico) no processo de compostagem doméstica.
Palavras-chave em português
Análise térmica
Biodegradação
Biopolímeros
Compostagem
Difração de raios X
Espectroscopia Raman
Poliéster
Sacolas de supermercado
Resumo em português
Neste trabalho, foram estudadas blendas de poliésteres sintéticos e de fonte renovável - poli(tereftalato de butileno-co-adipato de butileno) - PBAT e poli(ácido láctico) - PLA, respectivamente, utilizados em sacolas de supermercado. Amostras destes materiais foram pesadas e enterradas em solo simulado por quatro meses para simular uma compostagem tradicional. As amostras foram então analisadas por Calorimetria Exploratória Diferencial (DSC), Termogravimetria e Termogravimetria Derivada (TG e DTG, incluindo uma Análise Cinética não isotérmica comparativa com sacolas de PE aditivadas com agente pró-degradante, Espectroscopia Vibracional Raman com Transformada de Fourier (FT-Raman), Difração de Raios X e Cromatografia de exclusão por tamanho. Embora não tenha havido perda de massa significativa no período do envelhecimento por compostagem tradicional, foram constatadas importantes alterações estruturais nas amostras, tais como a redução nas energias de ativação (Ea) para os processos de decomposição térmica, a redução na intensidade da banda relativa ao estiramento da carbonila presente nos poliésteres e também uma drástica redução da massa molecular dos polímeros. Em paralelo, a aceleração do processo de biodegradação com Vermicompostagem foi investigado, com resultados bastante promissores, incluindo a degradação total da amostra após um tratamento prévio de exposição à luz solar.
Título em inglês
Study about the partial degradation of poly(butylene adipate-co-terephthalate) and poly(lactic acid) blends in the process of Home Composting.
Palavras-chave em inglês
Biodegradation
FT-Raman
Shopping plastic bags
Thermal analysis
WAXD
Resumo em inglês
In this study, blends of the synthetic polyester poly(butylene adipate-cotherephtalate) - PBAT - and the natural one poly(lactic acid) - PLA - used as biodegradable plastic shopping bags were studied. Samples of these materials were weighed and buried in simulated soil for four months to simulate domestic composting. These samples were then studied by Differential Scanning Calorimetry (DSC), Thermogravimetry (TG, including a comparative non-isothermal Kinetic Analysis with PE shopping bags containing prodegradation agents), Transformed Fourier Raman Vibrational Spectroscopy (FT-Raman), Wide Angle X-Ray Diffraction (WAXD) and Gel Permeation Chromatography (GPC). It was observed that even though there was no significant mass loss in the period of the ageing when using conventional home composting, important structural changes were detected in the samples, such as the reduction of activation energies (Ea) for the thermal decomposition processes, the reduction of intensity of the peak associated with the stretching of the carbonyl present in both polyesters and also a dramatic decrease in molecular weights. In parallel, the acceleration of the biodegradation process with vermicomposting was investigated, with very promising results, including the total disintegration of the samples when submitted to a previous treatment of sun light exposure.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2016-11-10
 
AVISO: O material descrito abaixo refere-se a trabalhos decorrentes desta tese ou dissertação. O conteúdo desses trabalhos é de inteira responsabilidade do autor da tese ou dissertação.
  • ARAUJO JR, J., et al. COMPARATIVE THERMAL DEGRADATION OF BIODEGRADABLE AND OXO-DEGRADABLE POLYMERIC BLENDS USED IN SHOPPING BAGS IN BRAZIL. journal of chemical, biological and physical sciences, 2013, vol. 3, p. 2895-2901.
  • ARAUJO JR, J., et al. PBAT-PLA BLENDS BURIED IN SIMULATED SOIL:CHARACTERIZATIONBY DIFFERENCIAL SCANNING CALORIMETRY,RAMANSPECTROSCOPY AND WIDE ANGLE X-RAY DIFFRACTION. JOURNAL OF CHEMICAL, BIOLOGICAL AND PHYSICAL SCIENCE, 2013, vol. 3, p. 2858-2866.
  • ARAUJO JR, J., e WIEBECK, H. sacolas plásticas biodegradáveis- uma parte da solução para o problema dos resíduos sólidos nos assentamentos humanos. Assentamentos Humanos (Marília) [online], 2011, vol. 13, p. 79-85. Dispon?vel em: http://www.universidade de marilia.com.br.
  • ARAÚJO, J., et al. Thermal Degradation and Kinetic Parameters of Polyester and Poly(Lactic Acid) Blends Used in Shopping Bags in Brazil [doi:10.1007/s10924-013-0632-9]. Journal of Polymers and the Environment [online], 2014, vol. 22, p. 52-57.
  • ARAUJO JR, J., et al. ESTUDO TERMOANALÍTICO DE BLENDAS DE POLIÉSTER E POLI(ÁCIDO LÁCTICO) UTILIZADAS EM SACOLAS BIODEGRADÁVEIS DE SUPERMERCADO. In VIII CONGRESSO BRASILEIRO E III CONGRESSO PAN-AMERICANO DE ANÁLISE TÉRMICA E CALORIMETRIA, CAMPOS DO JORDÃO, 2012. VIII CONGRESSO BRASILEIRO E III CONGRESSO PAN-AMERICANO DE ANÁLISE TÉRMICA E CALORIMETRIA., 2012. Dispon?vel em: http://WWW.ABRATEC.COM.BR.