Tesis Doctoral
DOI
https://doi.org/10.11606/T.3.2013.tde-09072014-115609
Documento
Autor
Nombre completo
Renata Andrade Kobayashi Cavalcante
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2013
Director
Tribunal
Toffoli, Samuel Márcio (Presidente)
Espinosa, Denise Crocce Romano
Martinelli, José Roberto
Silva, Davinson Mariano da
Valenzuela Díaz, Francisco Rolando 1952-
Título en portugués
Estudo do efeito de compostos de selênio em vidros soda-cal-sílica.
Palabras clave en portugués
Método sol-gel
Microencapsulação
Rendimento do selênio
Vidro soda-cal-sílica
Resumen en portugués
O selênio é utilizado como elemento colorante ou descolorante na indústria vidreira. Sua característica altamente volátil durante a fusão do vidro, com perdas de até 80%, tem sido uma questão discutida já há muito tempo. Assim, alternativas têm sido buscadas na tentativa de aumentar o rendimento do selênio. Utilizar o princípio da microencapsulação do selênio através da obtenção de vidros pelo método sol-gel apresenta-se como uma possibilidade para novos estudos. O método sol-gel permite obter vidros de alta pureza utilizando recursos mais simples que em uma fusão convencional. Este trabalho apresenta um estudo do rendimento do selênio em duas composições de vidros sodo-cálcicos. Para tanto, foram utilizadas diferentes fontes de selênio (Se0, ZnSeO3, Na2SeO3). Uma proposta desta pesquisa foi obter uma nova fonte de selênio através da síntese de um material rico em sílica pelo método sol-gel, o qual contenha selênio em sua formulação. Este material é utilizado como uma alternativa de inserção de selênio visando o aumento de seu rendimento durante a fusão, considerando-se o princípio da microencapsulação. As amostras vítreas contendo selênio apresentaram coloração rosa. Os resultados de análise química mostram que a incorporação de selênio foi maior para as amostras com maior concentração de álcalis. Uma das amostras contendo um dos materiais sintetizados pelo método sol-gel apresentou a menor perda de selênio (34%) dentre todas, indicando que o método proposto foi eficiente para a redução da volatilização deste elemento. Os ensaios de absorção óptica apresentam três bandas de absorção: 380 nm (Fe3+), 500 nm (Se0 / Se2-) e 720 nm (Fe2+). As amostras obtidas por sol-gel são amorfas, adquiriram uma forte coloração avermelhada com o tempo e os resultados obtidos nos ensaios de caracterização indicaram uma potencial aplicação deste material como sensor de umidade.
Título en inglés
Study of the effect of selenium compounds in soda-lime-silica glasses.
Palabras clave en inglés
Microencapsulation
Selenium yield
Soda-lime-silica glass
Sol-gel method
Resumen en inglés
Selenium is used as a colorant and discolorant element in the glass industry. Its highly volatile characteristic during the glass melting, which causes losses around 80%, has been discussed for a long time. Meanwhile, alternatives have been searched to increase the yield of selenium. Microencapsulation of the selenium by sol-gel processing may be considered for new studies. This work presents an investigation, in laboratory scale, of the selenium yield in two model soda-lime glass compositions. Different sources of selenium (Se0, ZnSeO3, Na2SeO3) were used, which were incorporated into a silica rich material, containing the selenium source, by sol-gel method. The glass samples were obtained by melting the raw-materials at 1350°C in high alumina crucibles, and showed different grades of pink coloration. Chemical analysis results showed that the incorporation of selenium was higher in the glass containing higher concentration of alkaline elements. In terms of selenium source, the best yield (lowest loss of selenium) was 34 wt%, obtained with SG3 (synthesized material by sol-gel method) as the selenium source. The optical absorption curves presented three main absorption bands: 380 nm (Fe3+), 500 nm (Se0/Se2-) and 720 nm (Fe2+). The samples obtained by sol-gel were amorphous, acquired a strong reddish coloration with time, and indicated potential characteristics for application as a humidity sensor.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fichacatalografica.doc (33.00 Kbytes)
Tese_RAKC2013.pdf (2.50 Mbytes)
Fecha de Publicación
2014-07-14
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.