Tese de Doutorado
Documento
Autor
Nome completo
Marcos Gonzales Fernandes
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2017
Orientador
Banca examinadora
Wiebeck, Hélio (Presidente)
Cortés, Guillermo Ruperto Martín
Diaz, Francisco Rolando Valenzuela
Esper, Fábio José
Silva, Leonardo Gondim de Andrade e
Título em português
Obtenção de nanocompósitos de borracha natural e organoargila com variação no processo de organofilização.
Palavras-chave em português
Argilas
Borracha
Nanocompósitos
Resumo em português
Foi preparado o nanocompósito de borracha natural/argila chocolate B modificada por sodificação via seca com variação no processo, utilizando silicato de sódio ao invés de carbonato de sódio e tratada com sal quaternário de amônio, cloreto hexadecil trimetil amônio. A argila no seu estado natural, após sodificação e após quaternização foi caracterizada pelas técnicas de microscopia estereoscópica, análise térmica, infravermelho, difração de raios X e microscopia eletrônica de varredura. Outras cargas orgânicas foram adicionadas, como celulose e piaçava e comparadas com cargas tradicionais, como o negro de fumo. As placas obtidas, após vulcanização, tiveram medidas as suas propriedades mecânicas e foram analisadas por DRX e MEV. Os nanocompósitos obtidos mostraram melhoria nas suas propriedades mecânicas em comparação com as placas sem a adição de argila.
Título em inglês
Making natural rubber-organoclay nanocompósites with variation in the organophilization process.
Palavras-chave em inglês
Nanocomposites
Natural rubber
Natural rubber nanocomposites
Organophilic clays
Resumo em inglês
The natural rubber/clay chocolate B nanocomposite modified by dry sodification process with variation processing was prepared using sodium silicate instead of sodium carbonate and treated with quaternary ammonium salt, hexadecyl trimethyl ammonium chloride. The clay in its natural state after sodification and after quaternization was characterized by the techniques of stereoscopic microscopy, thermal analysis, infrared, X-ray diffraction and scanning electron microscopy. Other organic fillers were added, such as cellulose and piaçava, and compared with traditional fillers such as carbon black. The plates obtained after vulcanization had their mechanical properties measured and were analyzed by XRD and SEM. The obtained nanocomposites showed improvement in their mechanical properties in comparison with the plates without the addition of clay.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2017-11-09
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2014. Todos os direitos reservados.