Master's Dissertation
DOI
https://doi.org/10.11606/D.3.2016.tde-05012016-155251
Document
Author
Full name
Daniel Augusto Ferro
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2015
Supervisor
Committee
Plaut, Ronald Lesley (President)
Lima, Nelson Batista de
Schön, Claudio Geraldo
Title in Portuguese
Caracterização e estampabilidade de um aço SAE 1080 fosfatizado.
Keywords in Portuguese
Aço
C80U modificado
CLC
Conformação mecânica
Curva limite de conformação
Ensaio Nakazima
Fosfato de zinco
Propriedades dos materiais
Abstract in Portuguese
Devido a crescente necessidade de elevação dos níveis de conformação em peças estampadas em geral, existe uma demanda cada vez maior em ligas e processos diversificados que atendam as variadas exigências do setor de produtos estampados e posteriormente tratados termicamente para aumento de dureza. Desse modo desenvolveu-se a liga C80U modificada, que é uma variante da liga C80U especificada na norma DIN EN ISO 4957 porém com adição de Cromo, entretanto a liga C80U modificada ainda é pouco estudada e pouca informação técnica se tem a seu respeito. Com a finalidade de melhor conhecimento técnico dessa liga, foram conduzidos estudos de caracterização em amostras laminadas a quente e após processo de esferoidização posteriormente sendo revestidas com fosfato de zinco. Foram realizados estudos de composição química, microestrutura, textura cristalográfica, propriedades mecânicas e estrutura do fosfato, além de levantamento da curva CLC através do método Nakazima e evolução da rugosidade 2D e 3D em amostras com e sem revestimento de fosfato, antes e após conformação. Através dos resultados parciais encontrados, foi possível definir o lado da curva CLC relacionado ao estiramento da chapa bem como comparar o deslocamento e a força do punção no teste Nakazima conformando-se amostras esferoidizadas sem revestimento e com revestimento de fosfato.
Title in English
Characterization and stampability of SAE 1080 phosphatized steel.
Keywords in English
C80U modified
FLD
Forming limit diagram
Nakazima test
Zinc phosphate
Abstract in English
Due to the increasing demand for enhanced formability levels of stamped parts in general, there is also an increasing demand for various alloys and processes that comply with the various requirements associated with stamped products that are subsequently heat treated to increase their hardness. Along this line, a modified C80U alloy has been developed, which is a variant of the alloy C80U specified in the standard DIN EN ISO 4957 but with the addition of Chrome. However, this alloy is still poorly studied and little technical information is available about it. In order to increase the knowledge of this alloy, characterization studies were conducted on hot rolled, after spheroidization and subsequently coated with zinc phosphate samples. The studies performed included chemical composition, microstructure, crystallografic texture, mechanical properties and analysis of the phosphate structure, as well as Nakazima tests in order to obtain the forming limit diagram (FLD) curve and the 2D and 3D roughness evolution of spheroidized samples coated and uncoated before and after the stamping process. Through the partial results obtained, it was possible to define the side of FLD curve related to stretching of the sheet as well as comparing the displacement and force of the punch on Nakazima test, stamping spheroidized samples both uncoated and coated with zinc phosphate.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2016-01-13
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2024. All rights reserved.