Dissertação de Mestrado
DOI
https://doi.org/10.11606/D.3.2018.tde-04102018-081012
Documento
Autor
Nome completo
Raphael Cons Andrades
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2018
Orientador
Banca examinadora
Diaz, Francisco Rolando Valenzuela (Presidente)
Júnior, Antônio Hortêncio Munhoz
Neves, Roberto de Freitas
Título em português
Sí­ntese de zeólita A e aplicação em adsorção de metais pesados.
Palavras-chave em português
Adsorção
Caulim
Metais pesados
Síntese hidrotermal
Zeólita A
Resumo em português
Este trabalho objetivou estudar a síntese de zeólita NaA sob condições hidrotérmicas e aplicála na adsorção de metais pesados. Para a síntese de zeólita NaA, caulim do município de Ipixuna, Pará, foi calcinado a 700 °C por 3 horas para obtenção de metacaulim e usado como fonte de sílica e alumina. Para efeito de comparação, cloreto de alumínio e metassilicato de sódio também foram utilizados na síntese de zeólitas como precursores de Si e Al. A influência da alcalinidade na síntese dos produtos zeolíticos foi avaliada utilizando-se diferentes concentrações de NaOH. Todas as sínteses foram realizadas a 110 °C em autoclaves. Visando à compreensão da influência do tempo na quantidade e tipo de fase formada, foram realizadas sínteses com diferentes tempos de cristalização. Os produtos de reação foram caracterizados por difração de raios X, espectroscopia na região do infravermelho, análise termogravimétrica, análise térmica diferencial, microscopia eletrônica de varredura e adsorção de nitrogênio para cálculo de área específica pelo método BET. A amostra que apresentou maior proporção de zeólita NaA foi utilizada como adsorvente em soluções de Cu2+, Ni2+ e Cd2+ com concentrações iniciais de 25 a 400 mg/L. A concentração de equilíbrio desses metais, após remoção pela zeólita NaA, foi determinada por espectrofotometria de absorção atômica. Os resultados mostraram que o aumento da alcalinidade e do tempo de cristalização favoreceu a obtenção de sodalita, uma fase zeolítica concorrente à Zeólita A, nos produtos de síntese. A zeólita NaA provou ser um excelente adsorvente para remoção dos metais analisados, apresentando uma capacidade de adsorção máxima de aproximadamente 79, 65 e 32 mg/g para Cd2+, Cu2+ e Ni2+, respectivamente. O modelo de isoterma de adsorção que melhor descreveu a remoção de metais pela zeólita NaA foi o de Langmuir.
Título em inglês
Synthesis of Zeolite A and application in adsorption of heavy metals.
Palavras-chave em inglês
Adsorption
Heavy metals
Hydrothermal synthesis
Kaolin
Zeolite A
Resumo em inglês
The aim of this work was to study the synthesis of zeolite NaA under hydrothermal conditions and use it as adsorbent of heavy metals. To synthesize zeolite NaA, kaolin from the city of Ipixuna, Pará, was calcined at 700 °C for 3 hours and used as source of silica and alumina. For comparison purposes, aluminum chloride and sodium metasilicate were also used in the synthesis of zeolites as precursors of Si and Al. The influence of alkalinity on the synthesis of the zeolitic products was evaluated using different NaOH concentrations. All the syntheses were performed at 110 °C by autoclaving. To understand the influence of time on the type and relative amount of the obtained phases, syntheses with different crystallization times were carried out. The reaction products were characterized by means of X-ray diffraction, infrared spectroscopy, thermogravimetric analysis, thermal differential analysis, scanning electron microscopy and nitrogen adsorption for calculating surface area by the BET method. One of the samples, which exhibited the highest content of zeolite NaA, was used as adsorbent of Cu2+, Ni2+ and Cd2+ solutions with initial concentrations ranging from 25 to 400 mg/L. The equilibrium concentration of these heavy metals, after removal by zeolite NaA, was determined by atomic absorption spectrophotometry. The results showed that increasing alkalinity of the reaction medium led to the formation of sodalite, a concurrent zeolitic phase, in the products. Zeolite NaA turned out to be an excellent adsorbent for removing heavy metals, with an adsorption capacity of 79, 65 and 32 mg/g for Cu2+, Cd2+ and Ni2+, respectively. The Langmuir isotherm model was the most appropriate to describe the removal of metals by zeolite A.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2018-10-09
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2024. Todos os direitos reservados.