Tesis Doctoral
DOI
https://doi.org/10.11606/T.3.2009.tde-02092009-142824
Documento
Autor
Nombre completo
Freddy Poetscher
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2009
Director
Tribunal
Brandi, Sérgio Duarte (Presidente)
Azevedo, Cesar Roberto de Farias
Ramalho, José Pinto
Schön, Cláudio Geraldo
Silva, Pedro Miguel dos Santos Vilaça da
Título en portugués
Efeito do número de passes e do tratamento térmico pós-soldagem de liga de alumínio AA 6063 soldada por atrito linear com mistura (FSW).
Palabras clave en portugués
Alumínio
Soldagem no estado sólido
Soldagem por atrito linear com mistura (SALM)
Soldagem por FSW
Resumen en portugués
O processo de soldagem por atrito linear com mistura (FSW) é uma técnica recente para a soldagem no estado sólido de materiais, em particular para o alumínio e suas ligas. O processo foi inventado na Inglaterra em 1991. Neste processo, as partes a serem soldadas são fixadas e uma ferramenta especial realiza a soldagem de forma contínua. A ferramenta possui uma velocidade de rotação e, durante a sua translação, o material é misturado no estado sólido e, conseqüentemente, soldando as duas partes. A junta soldada por FSW de alumínio AA 6063-T6, com espessura de 3 mm foi caracterizada. A soldagem foi realizada com uma rotação da ferramenta de 710 rpm e com uma velocidade de translação de 5,3 mm/s. A ferramenta empregada é do tipo three flats, com diâmetro do ombro de 14 mm, diâmetro do pino de 3 mm e com ângulo de 90° com relação à horizontal. Os corpos de prova foram soldados em três condições: um passe, dois passes e dois passes com inversão de rotação do pino. Após a soldagem foram realizados os seguintes tratamentos térmicos: solubilização, envelhecimento e recozimento. A junta soldada foi caracterizada por macrografias, micrografias, microdureza, ensaios de calorimetria diferencial e EBSD. Os resultados mostraram que existem ZTMAs diferentes conforme a condição dos de passes. O número de passes tem influência nas componentes da textura alterando de Cubo para Latão e para Goss + Cobre. Os tratamentos térmicos de envelhecimento e recozimento produziram as maiores e menores durezas do cordão, respectivamente. Foi observada a sinergia entre os fatores número de passes e região do cordão no tamanho de grão do cordão. O lado de retrocesso, após o tratamento térmico, apresentou os grãos mais finos.
Título en inglés
Effect of multipass FSW welding of aluminum AA6063 and heat treating after welding.
Palabras clave en inglés
Aluminium
Friction stir welding (FSW)
Solid state welding
Resumen en inglés
Friction stir welding (FSW) is a recent process for aluminium welding in solid state. This process was invented in England in 1991. The welding process is done with a special rotating tool that travels along the joint while the parts are fixed. The tool has a speed and a rotation and during its translation the material mixtures in solid state and the joint occurs. The objective of this paper is to show the metallurgical and mechanical characteristics of a 3 mm thick Aluminum AA 6063 T6 plate welded joint. The tool rotation speed was 710 rpm and the translation speed was 5.3 mm/s. The type of the tool used was three flats, with a shoulder diameter of 14mm and pin diameter of 3mm and perpendicular to the plate. The samples were welded in three conditions: one pass, two passes and two passes with pin rotation inversion in the second pass. The welded samples were also submitted to solution heat treatment, solution heat treatment followed by aging and annealing heat treatments. The welded joint was studied with these main experimental techniques: optical and scanning electron microscopy, microhardness, differential scanning calorimetry and electron backscatter diffraction for texture analysis. The results showed different TAZs according to the welding conditions. The number of passes has influence over the texture components changing from Cube to Brass and to Goss + Copper. The aging and solution heat treatments showed the highest and the lowest hardness, respectively. Synergy between the welding conditions and weld region was observed for the grain size results. The retreating side produced the finest grains after heat treating.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-09-11
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.