Mémoire de Maîtrise
DOI
10.11606/D.3.2017.tde-02032017-144335
Document
Auteur
Nom complet
Ana Paula Gonçalves Chaves
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2016
Directeur
Jury
Goldenstein, Helio (Président)
Franco, Luiz Alberto Pereira das Neves
Alves, Luiz Henrique Dias
Titre en portugais
Rodas ferroviárias: análise, microestrutura e propostas de melhoria.
Mots-clés en portugais
Aço
Desgaste
Distância interlamelar da perlita
Ferrovias
Mudança de fase
Rodas
Trilhos
Resumé en portugais
A pesquisa relativa ao transporte ferroviário no Brasil tem se intensificado nos últimos anos visando principalmente a melhoria no desempenho do par rodatrilho. Isso se deve à demanda de se transportar cada vez mais carga por eixo com a finalidade de reduzir o custo de transporte. Através de mudanças na microestrutura do material ou de mudanças na composição das ligas utilizadas na fabricação pode se aumentar a resistência do par roda-trilho. Neste trabalho foi analisada a influência de diferentes microestruturas (puramente perlíticas e perlíticas-bainíticas), obtidas por meio de tratamento térmico por dilatometria, nas propriedades de um aço alto carbono similar ao utilizado em rodas convencionais classe C AAR destinadas ao transporte de carga pesada. As análises empregaram técnicas metalográficas (identificação de fases presentes e distância interlamelar da perlita), ensaios magnéticos (saturação magnética e ruído magnético de Barkhausen), ensaio mecânico de dureza e ensaio tribológico de resistência ao desgaste por deslizamento. Foram caracterizadas rodas ferroviárias classe C AAR em quatro condições distintas: usadas e novas, fundidas e forjadas.
Titre en anglais
Railway wheels: analysis, microstructure and improvement proposals.
Mots-clés en anglais
Pearlite interlamellar spacing
Railway wheels
Sliding wear
Resumé en anglais
Research about rail transport in Brazil has been intensified recently due the need to improve the wheel-rail performance, considering the demand of increasing axle load aiming for transportation cost reduction. Changes in the material microstructure or in the alloys composition can improve the wheel-rail resistance. A eutectoid steel similar to that used in conventional class C AAR wheels (designed to heavy haul transportation - high loads and low speeds) was submitted to isothermal heat treatments applying dilatometry techniques at ten different cycles. Different microstructures (totally pearlitic and pearlitic-bainitic) were obtained and their influence on the mechanical and magnetic properties was analyzed. The analysis included metallographic techniques (identification of phases and pearlite interlamellar spacing), magnetic testing (magnetic saturation and magnetic Barkhausen noise) and mechanical testing (hardness and pin-ondisc tests). Railway wheels Class C ARR were characterized in four different conditions: new and used, cast and forged.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2017-03-06
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.