Tesis Doctoral
DOI
10.11606/T.3.2001.tde-02012002-175418
Documento
Autor
Nombre completo
Antonio José Ramírez Londoño
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2001
Director
Tribunal
Brandi, Sergio Duarte (Presidente)
Modenesi, Paulo Jose
Monteiro, Waldemar Alfredo
Taniguchi, Celio
Tschiptschin, Andre Paulo
Título en portugués
Precipitação de fases intermetálicas e austenita secundária na ZAC de soldagens multipasse de aços inoxidáveis duplex.
Palabras clave en portugués
aço inoxidável duplex
austenita secundária
nitreto de cromo
soldagem multipasse
zona afetada pelo calor (ZAC)
Resumen en portugués
Os aços inoxidáveis duplex (AIDs) são materiais com um excelente desempenho tanto mecânico como à corrosão. Inúmeras pesquisas tem sido desenvolvidas para aprimorar a soldabilidade destas ligas. Algumas transformações de fase, que são passíveis de ocorrer durante o processo de soldagem, podem prejudicar seriamente o desempenho das juntas. Foram simuladas microestruturas da região da zona afetada pelo calor submetida a temperaturas elevadas (ZACTE), utilizando um modelo proposto de fluxo de calor. Abordaram-se aspectos fundamentais da precipitação de austenita secundária, de nitreto de cromo e as suas interações na ZACTE de soldas multipasse. Finalmente, foram realizados testes de tenacidade e de resistência à corrosão para avaliar o efeito das transformações de fase estudadas no desempenho das juntas soldadas. Os tratamento térmicos e simulações da ZACTE foram realizadas num equipamento GleebleÒ. As microestruturas foram analisadas mediante microscopia ótica e eletrônica de varredura e de transmissão. Junto com a microscopia eletrônica foram realizadas microanálises químicas das fases estudadas. Baseando-se nos resultados obtidos, verificou-se que nem todos os AIDs são susceptíveis de ferritizar. Este fato tem uma grande influência no comportamento metalúrgico e na soldabilidade destes aços. Quanto aos aspectos fundamentais da metalurgia destes aços, observou-se uma estreita interação entre a precipitação da austenita secundária e os nitretos de cromo, chegando-se a propor um mecanismo de nucleação da austenita secundária intragranular a partir dos nitretos. Por último, foi constatado que o efeito deletério da austenita secundária intragranular na resistência à corrosão pode ser evitado mediante a adequada elaboração do procedimento de soldagem.
Título en inglés
Intermetallic phases and secondary austenite precipitation at the multipass welding HAZ of duplex stainless steels.
Palabras clave en inglés
chromium nitride
duplex stainless steel
heat-affected zone (HAZ)
multipass welding
secondary austenite
Resumen en inglés
Duplex stainless steels (DSS) have excellent mechanical and corrosion properties. Many researches have been developed regarding the weldability of these alloys. There are some phase transformations that take place during the welding process, which may impair the welded joint behavior. High temperature heat-affected zone (HTHAZ) microstructures were simulated using a proposed heat flow model. Fundamental aspects of the secondary austenite and chromium nitride precipitation, and its interactions in the HTHAZ of multipass welds, were studied. In addition, toughness and corrosion tests were done to evaluate the influence of the studied phase transformations on the weld behavior. A GleebleÒ system was used to do the heat treatments and HTHAZ simulations. The microstructures were analyzed by means of optic and electron microscopy. Along with the electron microscopy it was done chemical microanalysis of the studied phases. Based on results, it was verified that not all DSSs can be ferritized. This fact has a strong influence on metallurgical behavior and weldability of these alloys. Regarding to the metallurgical fundamental aspects of these steels, it was observed a remarkable interaction between secondary austenite and chromium nitride precipitation. Thus, it was proposed a mechanism of intragranular secondary austenite precipitation from chromium nitrides. It was also verified, how the deleterious effect of intragranular secondary austenite in the corrosion resistance can be avoided by means of appropriate welding procedures.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Antonio_Ramirez.pdf (27.09 Mbytes)
Fecha de Publicación
2002-07-25
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.