Thèse de Doctorat
DOI
10.11606/T.3.2007.tde-08052007-165239
Document
Auteur
Nom complet
Aloisio José Schuitek
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2007
Directeur
Jury
Sinatora, Amilton (Président)
Albertin, Eduardo
Machado, Izabel Fernanda
Mello, José Daniel Biasoli de
Silva, Carlos Henrique da
Titre en portugais
Estudo do comportamento de desgaste de materiais metálicos em riscamento circular.
Mots-clés en portugais
Abrasão
Adesão
Desgaste
Deslizamento
Oxidação
Transição
Resumé en portugais
Neste trabalho estudaram-se os mecanismos de desgaste predominantes no riscamento circular em materiais metálicos quando de uma transição do tipo de desgaste por deslizamento para o desgaste por abrasão. A técnica utilizada foi a esclerometria circular. Para fazer a função de elementos abrasivos, utilizou-se indentadores de rubi e diamante com geometrias semi-esféricas e em troncos de cone (essas para simular partículas abrasivas desgastadas). O principal material de contra-corpo analisado foi o aço 0,4 % C de baixa liga, com dureza de 48 HRc (temperado e revenido). Foram investigados também os comportamentos de desgaste do cobre eletrolítico, latão 360 (ASTM B-16), ligas de alumínio 2011-T3, 6061-T8, 6262-T8 e ferro fundido cinzento e vermicular. Os carregamentos normais utilizados foram reduzidos e dependentes da geometria dos indentadores utilizados, de forma a se iniciar o ensaio sempre em uma condição de deslizamento. As mudanças nos comportamentos de desgaste foram acompanhadas por alterações nas curvas de força de atrito em relação ao número de voltas do disco (ciclos). Identificaram-se três estágios bem distintos do comportamento de desgaste: Estágio I ou Desgaste ¨Zero¨, Transição e Estágio II ou Desgaste em Regime Permanente. Apenas a partir da Transição é que ocorrem desprendimentos sensíveis de material na forma de partículas de desgaste. No Estágio II, podem ocorrer todos os principais mecanismos de desgaste, ou seja, abrasão, oxidação, adesão, fadiga e um tipo específico, designado por desgaste por deformação plástica acumulada. A predominância de um em relação aos demais mecanismos de desgaste depende principalmente dos seguintes fatores de influência: material de ensaio, geometria do indentador, carga normal aplicada e meio interfacial.
Titre en anglais
Study of wear behavior of mettalic materials in circular scratching test.
Mots-clés en anglais
Abrasion
Adhesion
Oxidation
Sliding
Transition
Wear
Resumé en anglais
This work aimed at studying the wear mechanisms that prevail during circular scratch testing in metallic materials. The focus has been to understand the transition region between the sliding wear to the abrasive wear. To that, the main approach has been to apply the circular sclerometric technique. To perform the function of abrasion (simulating the behavior of abrasive elements), indenters (made of ruby and diamond), with semi-spherical and sectioned cone tips were developed. This last type of tip aims at simulating worn abrasive particles. The low-alloy 0,4 %C steel, with 48 HRc (quenched and tempered) was the main material examined. Additionally, it has also been observed the wear behavior of the following materials: i/ electrolytic cooper; ii/ brass alloy 360 (ASTM B-16); iii/ aluminium alloys 2011-T3, 6061-T8, 6262-T8; iv/ grey cast iron; and v/ vermicular cast iron. The normal loads were adjusted, considering the geometry of the indenter, thus the specimen test would always start obeying a sliding condition. The changes in the wear behavior in a scratch testing were followed through the variations in the curves of friction force curves versus the number of turns in the disc (cycles). Three well defined wear behavior stages were identified: i/ Stage I or Zero Wear; ii/ Transition; and iii/ Stage II or Wear in Steady State. It was only from the transition stage that perceptible material detachments occurred in the form of wear debris. During Stage II all the foreseeable wear mechanisms (i.e. abrasion, oxidation, adhesion, fatigue and a specific type, named by cumulative plastic deformation) can take place. The predominance of one wear mechanism despite the others depends on: i/ testing materials; ii/ indenter's geometry; iii/ normal load applied; iv/ interfacial films conditions.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
01INTRODUCAO.pdf (62.61 Kbytes)
03OBJETIVOSDATESE.pdf (38.06 Kbytes)
09REFERENCIAS.pdf (92.28 Kbytes)
fichacatalografica.pdf (31.95 Kbytes)
Date de Publication
2007-06-05
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.