Disertación de Maestría
DOI
10.11606/D.3.2006.tde-05092006-131535
Documento
Autor
Nombre completo
John Ferney Alvarez Rosário
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2006
Director
Tribunal
Souza, Roberto Martins de (Presidente)
Machado, Izabel Fernanda
Silva, Marcio Bacci da
Título en portugués
Avaliação da integridade da superfície no torneamento de um ferro fundido nodular com carboneto.
Palabras clave en portugués
carboneto
ferro fundido nodular
integridade da superfície
torneamento
Resumen en portugués
Neste trabalho, estudou-se a integridade superficial durante o torneamento de um ferro fundido nodular com carbonetos, considerando a heterogeneidade microestrutural (fração volumétrica, tamanho e morfologia de grafita e dos carbonetos) e os efeitos dos parâmetros de corte (avanço, velocidade de corte e profundidade de corte), baseados num planejamento fatorial fracionário 24-1. Este texto apresenta, numa primeira parte, uma revisão baseada em referências bibliográficas clássicas da engenharia de superfícies, na tentativa de definir os conceitos que compõem a integridade da superfície. Posteriormente, descrevem-se os resultados de ensaios preliminares, realizados com a finalidade avaliar os níveis do processo e os efeitos desses parâmetros na integridade da superfície. Finalmente, realizaram-se os ensaios de usinagem em corpos-de-prova de ferro fundido nodular com carboneto, nos diâmetros de 80 mm e 140mm. Durante os ensaios de torneamento empregaram-se duas velocidades de corte (60 m/min e 180 m/min), dois avanços (0,1 mm/rev e 0,3 mm/rev) e duas profundidades de corte (0,2 mm e 0,3 mm). Após os ensaios de usinagem, foram realizadas: a avaliação das propriedades do material usinado (dureza e microestrutura), a análise de topografia da superfície usinada mediante avaliação da rugosidade, e a avaliação da influência dos parâmetros de usinagem na rugosidade. Encontrou-se uma dependência estatisticamente significativa da variação nas propriedades mecânicas dos corpos-de-prova em função da microestrutura, e mostraram-se os efeitos dessas variações em termos da integridade da superfície usinada.
Título en inglés
Assessment of surface integrity in turning of an ductile cast iron with carbides.
Palabras clave en inglés
carbide
ductile cast iron
surface integrity
turning
Resumen en inglés
In this work, the surface integrity of a ductile cast iron with carbides was studied during turning operations, considering the microstructural heterogeneity (volume fraction, size and morphology of the graphite and carbides) and the effect of the machining parameters (feed, cutting speed and depth of cut), based on a fractional factorial design 24-1. This work presents, initially, a literature review based on classic works on surface engineering, as an attempt to define the main concepts of surface integrity. Later, the results of preliminary test are described, which were conducted in order to define the process levels and the effects of these levels on the surface integrity. Finally, turning tests were conducted on specimens of ductile iron with carbides, at diameters of 80 and 140 mm. Two cutting speeds (60 m/min and 180 m/min), two feeds (0,1 mm/rev and 0,3 mm/rev) and two depths of cut (0,2 mm and 0,3 mm) were selected during the tests. Machined specimens were analyzed in terms of the properties of the machined material (hardness and microstructure) and of the roughness of the machined surface. The effect of the machining parameters on the roughness was also studied. A statistically significant dependence was observed for the properties of the machined specimens as a function of the microstructure and the effect of these properties on the surface integrity is presented.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2006-09-14
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.