Thèse de Doctorat
DOI
https://doi.org/10.11606/T.25.2003.tde-16082005-093342
Document
Auteur
Nom complet
Gildo Coelho Santos Júnior
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Bauru, 2003
Directeur
Jury
Rubo, Jose Henrique (Président)
Araújo, Roberto Paulo Correia de
Ferreira, Paulo Martins
Francisconi, Paulo Afonso Silveira
Mowafy, Omar El
Titre en portugais
Resistência à tração diametral de uma resina composta associada a pinos intra-radiculares pré-fabricados.
Mots-clés en portugais
pinos dentários
resinas compostas (resistência)
resistências a tração
Resumé en portugais
Este estudo teve a finalidade de verificar influência de diferentes tipos de pinos intra-radiculares sobre a resistência à fratura de um material restaurador coronário, utilizando o teste de tração diametral. Foram confeccionados 70 corpos de prova divididos em 7 grupos: G1. Compósito (Tetric Ceram – Ivoclar/Vivadent) (Grupo Controle); G2. Compósito e pino VectrisPost (Ivoclar/Vivadent); G3. Compósito e pino Fiber-Post (Jeneric/Pentron); G4. Compósito e pino Æstheti-Plus (Bisco); G5. Compósito e pino Light-Post (Bisco); G6. Compósito e pino Dentorama (Svenska) e G7. Compósito e pino ParaPost (Còltene/Whaledent). Todos os grupos foram submetidos ao ensaio de tração diametral em uma máquina de ensaios Instron, modelo 8501, até a fratura. A média dos grupos em MPa foi: G 1- 49,64 (3,36); G 2- 29,77 (3,36); G 3- 31,9 (2,39); G 4- 28,92 (2,20); G 5- 34,26 (3,37); G 6-33,45 (2,46) e G 7- 27,90 (2,40). A análise estatística dos dados nos permitiu concluir que: os pinos utilizados não reforçaram a resina composta; os pinos Light-Post, Dentorama e Fiber-Post apresentaram os melhores valores de adesividade ao material de reconstrução coronária e que o pino metálico ParaPost apresentou o menor valor de adesão à resina de reconstrução coronal.
Titre en anglais
Diametral tensile strength of a resin composite core bonded to prefabricated posts.
Resumé en anglais
The purpose of this study was to determine the influence of different types of posts on the fracture strength of a resin composite core material using the diametral tensile strength test. Seven groups of specimens were prepared each with 10 cylindrical specimens made of one composite material (Tetric Ceram, IvoclarVivadent) as follows: Group 1- Control group of composite only specimens; Group 2-Composite and VectrisPost (IvoclarVivadent); Group 3- Composite and Fiber-Post (Jeneric/Pentron); Group 4- Composite and Æstheti-Plus post (Bisco); Group 5- Composite and Light-Post (Bisco); Group 6- Composite and Dentorama post (Svenska) and group 7- Composite and ParaPost (Coltene/Whaledent). Following storage specimens were subjected to compressive loading in an Instron testing machine (model 8501) until failure occurred. Means and standard deviations of diametral tensile strengths in MPa were: Group 1- 49,64 (3,36); Group 2- 29,77 (3,36); Group 3- 31,9 (2,39); Group 4- 28,92 (2,20); Group 5- 34,26 (3,37); Group 6- 33,45 (2,46) and Group 7- 27,90 (2,40). Statistical analysis revealed significant differences in mean diametral tensile strengths among the groups. It is concluded that the use of posts did not reinforce the composite resin cores. Among the post/core groups Light-Post, Dentorama post and Fiber-Post resulted in the highest values of tensile strength while ParaPost resulted in the lowest value of tensile strength.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2005-08-22
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.