Tese de Doutorado
DOI
10.11606/T.25.2009.tde-30062009-150600
Documento
Autor
Nome completo
Adilson Yoshio Furuse
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
Bauru, 2009
Orientador
Banca examinadora
Mondelli, José (Presidente)
Francisconi, Paulo Afonso Silveira
Goes, Mario Fernando de
Lima, Jose Eduardo de Oliveira
Sundfeld, Renato Herman
Título em português
Influência do sistema fotoiniciador nas propriedades fisicoquímicas de resinas experimentais
Palavras-chave em português
Aminas
Bis-Fenol A-Glicidil Metacrilato
FTIR
Metacrilatos
Resinas compostas
Resumo em português
O objetivo deste trabalho foi avaliar a influência de diferentes aminas terciárias no grau de conversão, na contração de polimerização, na taxa de contração, na microdureza Knoop, na estabilidade de cor e na transmitância de luz de resinas experimentais, contendo, em peso, BisGMA e TEGDMA (3:1), 0,25% de canforquinona (CQ) e 1% de amina (DMAEMA, CEMA, DMPT, DEPT ou DABE). A influência de diferentes protocolos de fotoativação também foi investigada. O grau de conversão foi avaliado através de FTIR-ATR e a contração pelo método do disco aderido. A partir da diferenciação numérica dos dados de contração em relação ao tempo, obteve-se a taxa de contração de polimerização. A estabilidade de cor e a transmitância foram avaliadas em diferentes períodos de envelhecimento artificial. Os resultados foram avaliados pelos testes de ANOVA, Tukey e T3 de Dunnett (α = 0,05). As propriedades estudadas variaram em função da amina. O grau de conversão e a contração de polimerização variaram na sequência: CQ < DEPT < DMPT ≤ CEMA ≈ DABE < DMAEMA. O grau de conversão e a contração também foram influenciados pelo protocolo de fotoativação, sendo observadas correlações positivas entre o grau de conversão e a contração e entre o grau de conversão e a taxa de contração. A cor variou na sequência: DMAEMA < DEPT < DMPT < CEMA < DABE. A transmitância variou na sequência: DEPT ≈ DABE < DABE ≈ DMPT ≈ CEMA < DMPT ≈ CEMA ≈ DMAEMA, sendo mais evidente para o comprimento de onda de 400nm. Não foram observadas correlações entre o grau de conversão e as propriedades ópticas. A resina contendo DMAEMA apresentou maior grau de conversão, contração, taxa de contração e dureza, além de melhor estabilidade nas propriedades ópticas.
Título em inglês
Influence of the photoinitiator system on physical-chemical properties of experimental resins
Palavras-chave em inglês
Amines
Bisphenol A-Glycidyl Methacrylate
Composite resins
FTIR
Methacrylates
Resumo em inglês
The aim of this work was to evaluate de influence of different tertiary amines on degree of conversion (DC), shrinkage-strain, shrinkage-strain-rate, Knoop microhardness, and colour and transmittance stabilities of experimental resins containing BisGMA / TEGDMA (3:1 wt), 0,25wt% camphorquinone, 1wt% amine (DMAEMA, CEMA, DMPT, or DABE). Different light-curing protocols were also evaluated. DC was evaluated with FTIR-ATR and shrinkage-strain with the bonded-disc method. Shrinkage-strain-rate data were obtained from numerical differentiation of shrinkage-strain data with respect to time. Colour stability and transmittance were evaluated during different periods of artificial aging, according to ISO 7491:2000. Results were evaluated with ANOVA, Tukey and Dunnetts T3 tests (α = 0.05). The studied properties varied according to amines. DC and shrinkage-strain were maximum at the sequence: CQ < DEPT < DMPT ≤ CEMA ≈ DABE < DMAEMA. Both DC and shrinkage were also influenced by the curing protocol, with positive correlations between DC and shrinkage-strain and DC and shrinkage-strain-rate. Colour varied in the sequence: DMAEMA < DEPT < DMPT < CEMA < DABE. Transmittance varied in the sequence: DEPT ≈ DABE < DABE ≈ DMPT ≈ CEMA < DMPT ≈ CEMA ≈ DMAEMA, being more evident at the wavelength of 400nm. No correlations between DC and optical properties were observed. The resin containing DMAEMA showed higher DC, shrinkage-strain, shrinkage-strain-rate and microhardness, in addition with better optical properties.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
AdilsonYFuruse.pdf (44.90 Mbytes)
Data de Publicação
2009-07-02
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.