Tesis Doctoral
DOI
10.11606/T.25.2009.tde-30062009-150600
Documento
Autor
Nombre completo
Adilson Yoshio Furuse
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2009
Director
Tribunal
Mondelli, José (Presidente)
Francisconi, Paulo Afonso Silveira
Goes, Mario Fernando de
Lima, Jose Eduardo de Oliveira
Sundfeld, Renato Herman
Título en portugués
Influência do sistema fotoiniciador nas propriedades fisicoquímicas de resinas experimentais
Palabras clave en portugués
Aminas
Bis-Fenol A-Glicidil Metacrilato
FTIR
Metacrilatos
Resinas compostas
Resumen en portugués
O objetivo deste trabalho foi avaliar a influência de diferentes aminas terciárias no grau de conversão, na contração de polimerização, na taxa de contração, na microdureza Knoop, na estabilidade de cor e na transmitância de luz de resinas experimentais, contendo, em peso, BisGMA e TEGDMA (3:1), 0,25% de canforquinona (CQ) e 1% de amina (DMAEMA, CEMA, DMPT, DEPT ou DABE). A influência de diferentes protocolos de fotoativação também foi investigada. O grau de conversão foi avaliado através de FTIR-ATR e a contração pelo método do disco aderido. A partir da diferenciação numérica dos dados de contração em relação ao tempo, obteve-se a taxa de contração de polimerização. A estabilidade de cor e a transmitância foram avaliadas em diferentes períodos de envelhecimento artificial. Os resultados foram avaliados pelos testes de ANOVA, Tukey e T3 de Dunnett (α = 0,05). As propriedades estudadas variaram em função da amina. O grau de conversão e a contração de polimerização variaram na sequência: CQ < DEPT < DMPT ≤ CEMA ≈ DABE < DMAEMA. O grau de conversão e a contração também foram influenciados pelo protocolo de fotoativação, sendo observadas correlações positivas entre o grau de conversão e a contração e entre o grau de conversão e a taxa de contração. A cor variou na sequência: DMAEMA < DEPT < DMPT < CEMA < DABE. A transmitância variou na sequência: DEPT ≈ DABE < DABE ≈ DMPT ≈ CEMA < DMPT ≈ CEMA ≈ DMAEMA, sendo mais evidente para o comprimento de onda de 400nm. Não foram observadas correlações entre o grau de conversão e as propriedades ópticas. A resina contendo DMAEMA apresentou maior grau de conversão, contração, taxa de contração e dureza, além de melhor estabilidade nas propriedades ópticas.
Título en inglés
Influence of the photoinitiator system on physical-chemical properties of experimental resins
Palabras clave en inglés
Amines
Bisphenol A-Glycidyl Methacrylate
Composite resins
FTIR
Methacrylates
Resumen en inglés
The aim of this work was to evaluate de influence of different tertiary amines on degree of conversion (DC), shrinkage-strain, shrinkage-strain-rate, Knoop microhardness, and colour and transmittance stabilities of experimental resins containing BisGMA / TEGDMA (3:1 wt), 0,25wt% camphorquinone, 1wt% amine (DMAEMA, CEMA, DMPT, or DABE). Different light-curing protocols were also evaluated. DC was evaluated with FTIR-ATR and shrinkage-strain with the bonded-disc method. Shrinkage-strain-rate data were obtained from numerical differentiation of shrinkage-strain data with respect to time. Colour stability and transmittance were evaluated during different periods of artificial aging, according to ISO 7491:2000. Results were evaluated with ANOVA, Tukey and Dunnetts T3 tests (α = 0.05). The studied properties varied according to amines. DC and shrinkage-strain were maximum at the sequence: CQ < DEPT < DMPT ≤ CEMA ≈ DABE < DMAEMA. Both DC and shrinkage were also influenced by the curing protocol, with positive correlations between DC and shrinkage-strain and DC and shrinkage-strain-rate. Colour varied in the sequence: DMAEMA < DEPT < DMPT < CEMA < DABE. Transmittance varied in the sequence: DEPT ≈ DABE < DABE ≈ DMPT ≈ CEMA < DMPT ≈ CEMA ≈ DMAEMA, being more evident at the wavelength of 400nm. No correlations between DC and optical properties were observed. The resin containing DMAEMA showed higher DC, shrinkage-strain, shrinkage-strain-rate and microhardness, in addition with better optical properties.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
AdilsonYFuruse.pdf (44.90 Mbytes)
Fecha de Publicación
2009-07-02
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.