• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Tese de Doutorado
DOI
10.11606/T.25.2002.tde-10012005-102846
Documento
Autor
Nome completo
Oscar Barreiros de Carvalho Júnior
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
Bauru, 2002
Orientador
Banca examinadora
Freitas, Cesar Antunes de (Presidente)
Bonachela, Wellington Cardoso
Cruz, Carlos Alberto dos Santos
Francisconi, Paulo Afonso Silveira
Nunes, Osvaldo Benoni da Cunha
Título em português
Avaliação 'in vitro' da dureza superficial, da contração de polimerização e da rugosidade de 29 resinas compostas
Palavras-chave em português
polimerização
propriedades físico-químicas
resinas compostas
Resumo em português
Foram analisadas in vitro a dureza superficial, a contração de polimerização e a rugosidade de 29 resinas compostas. Foram confeccionados 3 corpos-de-prova para cada material, com fotopolimerização por 80 segundos; após mais 5 minutos, determinou-se a dureza superficial Rockwell 30T; os espécimes foram então armazenados em água desionizada, a 37ºC, durante 168 horas, quando nova leitura da dureza foi realizada. Para avaliação da contração de polimerização, foram confeccionados 5 corpos-deprova para cada material; cada resina era inserida em uma matriz metálica, com uma cavidade em forma de “meia cana”, cujas paredes das extremidades planas eram paralelas entre si, com fotopolimerização por 40 segundos; após 10 minutos, removia-se a amostra da matriz, cujo comprimento era medido para se estabelecer a contração inicial ocorrida; os espécimes eram então armazenados em estufa a 37ºC, durante 168 horas (1 semana), quando nova medida era tomada, para se determinar a contração final da resina. Os mesmos corpos-de-prova usados nos testes de dureza, após desgaste com lixas de papel até a de n.º 1.500, foram analisados num rugosímetro. Estatisticamente, todas as resinas mostraram aumento da dureza e da contração de polimerização, da medição imediata para a com 168 horas. Em termos globais, as que apresentaram os melhores resultados, analisando-se as três características simultaneamente, foram a Z-100 e a P-60, enquanto as com o pior desempenho foram a Solitaire e a Helioprogress.
Resumo em inglês
In vitro surface hardness, polimerization shrinkage and roughness of 29 composite resins were stablished. For each material, it were made 3 specimens, photocured by 80 seconds; 5 minutes later, Rockwell 30T surface hardness was determined; the specimens were then imersed in deionized water, at 37ºC by 168 hours, when a new evaluation of hardness was effectued. In evaluating polymerization shrinkage, 5 specimens were made for each material; each resin was inserted in a metallic matrix, in which there was a cavitiy with the shape of a hemi-cilinder, whose flat surfaces were paralel between itself, com photopolimerization for 40 seconds; 10 minutes later, the lenght was measured to determine the inicial shrinkage; specimes were then stored in a stove, at 37ºC for 168 hours, when a new length measuring was effectued to determine the final shrinkage. The same specimens used for hardness were abraded with sand paper (till 1,500 mesh) and evaluated for roughness with a rugosimeter. All resins showed an increase in hardness and in polymerization shrinkage, since the inicial evaluation to that effectued 168 hours later. In a global way, by a simultaneous analysis of the 3 characteristics, the best results were presented by Z-100 and P-60; Solitaire and Helioprogress had the worst performance.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2005-01-18
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.