Thèse de Doctorat
DOI
https://doi.org/10.11606/T.23.2012.tde-15012013-120551
Document
Auteur
Nom complet
George Taccio de Miranda Candeiro
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2012
Directeur
Jury
Gavini, Giulio (Président)
Caldeira, Celso Luiz
Medeiros, Igor Studart
Tanomaru Filho, Mario
Vale, Mônica Sampaio do
Titre en portugais
Avaliação da radiopacidade, escoamento, pH e da liberação de íons cálcio de um cimento endodôntico biocerâmico
Mots-clés en portugais
Escoamento
Liberação de íons Cálcio
Materiais Biocerâmicos
Materiais Odontológicos
pH
Radiopacidade
Resumé en portugais
O objetivo do presente trabalho foi avaliar as propriedades físico-químicas de um cimento endodôntico biocerâmico, Endosequence BC Sealer (Brasseler USA, Savannah, GA, EUA). Radiopacidade, escoamento, pH e liberação de íons cálcio (Ca2+) foram analisadas e os resultados foram comparados aos do cimento AH Plus (Dentsply De Trey Gmbh, Konstanz, Alemanha). A radiopacidade e o escoamento foram avaliados de acordo com as normas ISO 6876/2001. Para o teste de radiopacidade, anéis metálicos com 10 mm de diâmetro e 1 mm de altura foram preenchidos com os cimentos. O valor da radiopacidade foi determinado de acordo com a densidade radiográfica, representada em mm Al. A análise do escoamento foi feita com 0,05 mL de cada cimento colocados sobre uma placa de vidro. Outra placa de vidro, com 20 g, foi cuidadosamente colocada sobre o cimento e sobre esta um peso de 100 g, totalizando 120 g, que permaneceram por 7 minutos. Em seguida, foram medidos os diâmetros maiores e menores dos discos formados, sendo esta feita com um paquímetro digital. A liberação de íons cálcio (Ca2+) e o pH foram medidos nos períodos de 3, 24, 72, 168 e 240 horas, com o auxílio de um espectrofotômetro e pHmetro, respectivamente. Os resultados foram analisados estatisticamente pelos testes ANOVA e Tukey, sendo considerado significante quando p<0,05. O cimento biocerâmico analisado apresentou radiopacidade (3,84 mm Al) significantemente menor do que o AH Plus (6,90 mm Al). Foi observado que o cimentos Endosequence BC Sealer e o AH Plus apresentaram escoamentos de 26,96 mm e 21,17 mm, respectivamente (p<0,05). O cimento biocerâmico apresentou maior pH e maior liberação de íons cálcio (Ca2+) do que o cimento AH Plus (p<0,05). Concluiu-se que o cimento Endosequence BC Sealer apresentou valores de radiopacidade e de escoamento em concordância com as norma ISO 6876/2001. Os valores de pH e de liberação de íons cálcio (Ca2+) foram favoráveis para um cimento endodôntico.
Titre en anglais
Evaluation of Radiopacity, flow, pH and release of calcium ions of a bioceramic root canal sealer
Mots-clés en anglais
Bioceramic Material
Calcium Ions Release
Flow
pH
Radiopacity
Root Canal Cements
Resumé en anglais
The aim of the present study was to evaluate the physicochemical properties of a bioceramic root canal sealer, Endosequence BC Sealer. Radiopacity, pH, release of calcium ions (Ca2+) and flow were analyzed and the results were compared with AH Plus cement. Radiopacity and flow were evaluated according to ISO 6876/2001 standards. For the radiopacity analysis, metallic rings with 10 mm in diameter and 1 mm of thickness were filled with cements. The radiopacity value was determined according to radiographic density (mm Al). The flow test was performed with 0.05 mL of cement placed on a glass plate. A 120-g weight was carefully placed over the cement. The largest and smallest diameters of the disks formed were measured using a digital caliper. The release of Ca2+ and pH were measured at periods of 3, 24, 72, 168 and 240 hours, with spectrophotometer and pHmeter, respectively. Data were analyzed by ANOVA and Tukeys test (p<0.05). The bioceramic endodontic cement showed radiopacity (3.84 mm Al) significantly lower than that of AH Plus (6.90 mm Al). The pH analysis showed that Endosequence BC Sealer showed pH and release of Ca2+ greater than those of AH Plus (p<0.05), during the experimental periods. The flow test revealed that the BC Sealer and AH Plus presented flow 26.96 mm and 21.17 mm, respectively (p<0.05). Endosequence BC Sealer showed radiopacity and flow according to ISO 6876/2001 recommendations. The others physicochemical properties analyzed demonstrated favorable values for a root canal sealer.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2013-02-15
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.