Disertación de Maestría
DOI
https://doi.org/10.11606/D.23.2013.tde-16122013-193112
Documento
Autor
Nombre completo
Fernando Taddeo
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2013
Director
Tribunal
Medeiros, Igor Studart (Presidente)
Borges, Alexandre Luiz Souto
Daronch, Márcia
Título en portugués
Caracterização de filme vítreo, sinterizado com diferentes ciclos térmicos, depositado sobre substrato de Y-TZP e sua resistência de união imediata e após termociclagem a cimentos resinosos
Palabras clave en portugués
Adesão
Filme vítreo
Tratamento de superfície
Zircônia
Resumen en portugués
A zircônia estabilizada por ítria (Y-TZP) apresenta excelentes propriedades mecânicas; entretanto, sua microestrutura cristalina inerte faz com que tratamentos aplicados em porcelanas e vitrocerâmicas, como condicionamento com ácido fluorídrico e aplicação de compostos silânicos, sejam ineficazes para obter união aos cimentos resinosos. Neste trabalho, propõe-se uma alternativa para aumentar a reatividade da Y-TZP a cimentos resinosos por meio de um processo de modificação da superfície através da deposição de um filme vítreo. O objetivo deste estudo é, portanto, caracterizar um filme vítreo, sinterizado com diferentes ciclos térmicos, após deposição sobre Y-TZP (YZ 20/19, VITA Blocks Zahnfabrik, Bad Saackingen, Germany) e avaliar a resistência de união imediata e após ciclagem térmica (10.000 ciclos 5 e 55°C) a dois cimentos resinosos (Relyx Arc, 3M/ESPE, St. Paul, MN, USA e Rely-X U200 3M/ESPE, Neuss, Germany). A caracterização do filme foi efetuada por meio de microscopia eletrônica de varredura, para avaliar a morfologia; EDS (Espectroscopia por dispersão de energia), para estabelecer uma análise qualitativa e semi-quantitativa dos elementos químicos presentes e mensuração do ângulo de contato. Foram propostas as seguintes condições experimentais na superfície da YTZP: deposição dos filmes sinterizados à 700°C, 900°C ou ciclo de sinterização para o auto glaze; aplicação do primer contendo MDP (Alloy Primer, Kuraray Medical Inc, Kurashiki, Okayama, Japan); e silicatização da superfície (sistema Rocatec Soft, 3M/ESPE, St. Paul, MN, USA). Após o ensaio mecânico, o padrão de fratura foi avaliado por meio de microscopia óptica. Para os dados obtidos, o traço de Pillai (p = 0,00) mostrou que o tipo de tratamento empregado tem um efeito significativo sobre a resistência de união. Para determinar a diferença entre os grupos estudados foi aplicado um teste de comparações múltiplas (Tukey). O filme 900 apresentou maior resistência de união imediata (42,2 MPa), sendo este valor estatisticamente superior a silicatização (35,5 MPa) e MDP (28,0 MPa). Os resultados obtidos após termociclagem, mostram que o filme 900 novamente apresentou maior resistência de união (36,8 MPa) e também foi estatisticamente superior ao MDP (16,1 MPa) e silicatização (27,3MPa). A análise em microscópio estereoscópico demonstrou um padrão de fratura predominantemente coesiva na resina para microtração imediata para os grupos com deposição do filme vítreo e silicatizados. Para o MDP, o padrão de fratura foi, na sua maioria, do tipo mista. O ângulo de contato medido imediatamente após os tratamentos de superfície apresentou-se menor para os grupos com filme e silicatização e manteve-se com baixos valores somente para os grupos com filme após limpeza com álcool absoluto. A análise por EDS das superfícies dos filmes indicou a presença de silício nos diversos pontos analisados. Concluiu-se, deste modo, que a deposição do filme vítreo mostrou-se como um meio eficiente para promover uma forte e durável união com da Y-TZP com os cimentos resinosos, independente da temperatura de sinterização utilizada.
Título en inglés
Characterization of a glass film, sintered under different thermal cycles, and its bond strength to resin cements immediately and after thermocycling
Palabras clave en inglés
Adhesion
Glass film
Surface treatment
Zirconia
Resumen en inglés
The yttria stabilized zirconia (Y- TZP) has excellent mechanical properties, however its inert crystalline microstructure makes treatments applied in porcelain and glass ceramics, such as hydrofluoric acid etching and application of silane compounds, are ineffective for the union resin cements. In this work, we propose an alternative to increase the reactivity of the Y- TZP resin cement by a process of surface modification by depositing a glass film. The aim of this study is therefore to characterize a glass film, sintered with different thermal cycles, after deposition on Y- TZP (YZ - 20/19, VITA Blocks Zahnfabrik, Bad Saackingen, Germany) and to evaluate the bond strength immediately after thermocycling (10.000 cycles 5 and 55°C) to two resin cements (Relyx Arc, 3M/ESPE, St. Paul, MN, USA and Rely - X U200 3M/ESPE, Neuss, Germany). The characterization of the glass film was performed by means of scanning electron microscopy to assess the morphology, EDS (Energy Dispersive Spectroscopy), to establish a qualitative and semi-quantitative chemical elements and measuring the contact angle. Been proposed the following experimental conditions on the surface of YTZP: deposition of films sintering at 700°C, 900°C or sintering cycle for VM9 self glaze; primer containing MDP (Alloy Primer, Kuraray Medical Inc., Okayama, Okayama, Japan) and silica coating surface (Rocatec Soft, 3M/ESPE, St. Paul, MN, USA) . After mechanical testing, the fracture pattern was evaluated by light microscopy. For data, the trace of Pillai (p = 0.00) showed that the type of treatment used has a significant effect on the bond strength. To determine the difference between groups was applied multiple comparison test (Tukey). The 900 film showed higher bond strength immediately (42.2 MPa), and this value was statistically superior to silica coat (35.5 MPa) and MDP (28.0 MPa). The results obtained after thermocycling, show that 900 film again showed highest bond strength (36.8 MPa) and was also statistically superior to MDP (16.1 MPa) and silica coating (27.3 MPa). The analysis in stereoscopic microscopes showed a pattern of predominantly cohesive fracture in the resin for immediate microtensile for groups with film deposition and silica coat. In the MDP, the fracture pattern was mostly of the mixed type. The contact angle measured immediately after the surface treatments was lower for groups with film and silica coat and remained with low values only for groups with film after cleaning with absolute alcohol. Analysis by EDS surfaces of the films indicated the presence of silicon at the various points analyzed. It was concluded therefore that the glass film deposition proved to be an efficient way to promote a strong and durable bond with Y- TZP with resin cements, regardless of sintering temperature used.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-02-11
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.