Tese de Doutorado
DOI
10.11606/T.23.2005.tde-06062005-155036
Documento
Autor
Nome completo
Mauricio José Arrais
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2005
Orientador
Banca examinadora
Yamada, Roberto Nobuaki (Presidente)
Costa, Bruno
Dias, Reinaldo Brito e
Mathias, Alênio Calil
Sesma, Newton
Título em português
Estudo in vitro da deformação permanente em grampos a barra fundidos em ligas de cobalto-cromo e em titânio comercialmente puro, submetidos a testes de tensão-deformação.
Palavras-chave em português
Grampos dentários
Prótese parcial removível
Resumo em português
Foram realizados testes de inserção e remoção de grampos a barra em “I”, fundidos com liga de Cobalto-Cromo (CoCr) e com Titânio comercialmente puro (Ti). Foi utilizada uma máquina oscilante de teste para verificar o comportamento elástico destes grampos que atuaram sobre superfícies metálicas com graus de retenção de 0,25mm e 0,50mm. Dez grampos de CoCr e dez de Ti foram submetidos a 12.500 ciclos de teste (cada) sobre as superfícies metálicas. A ocorrência da deformação permanente dos grampos foi mensurada por meio de relógios comparadores colocados sobre as pontas dos retentores, sendo que a leitura destes relógios ocorreu a cada 500 ciclos. Os resultados desta pesquisa in vitro indicaram que, após os 12.500 ciclos, não foram observadas fraturas nos grampos. E ainda que os grampos feitos em liga de CoCr sofreram menores deformações permanentes do que os de Ti para ambas as retenções.
Título em inglês
Permanent deformation in vitro study of “I” bar clasps cast with cobalt-chromium alloy and commercially pure Titanium, submitted to tension-deformation trials.
Palavras-chave em inglês
Dental clasps
Denture partial removable
Resumo em inglês
Insertion and removal trials of “I” bar clasps cast with cobalt-chromium alloy and commercially pure Titanium were carried out. An oscillating trial machine was utilized to verify the elastic behavior of these clasps, which acted on metallic surfaces with 0.25mm and 0.50mm degrees of retention. Ten CoCr clasps and ten Ti clasps were submitted to 12,500 trial cycles (each) on the metallic surfaces. The permanent deformation of the clasps was measured b y comparative gauges placed on the tips of the clasps, and the reading of the gauges was carried out every 500 cycles. The results of this in vitro research showed that after the 12,500 cycles clasp fractures were not observed and that clasps made with CoCr alloy suffered less permanent deformation than Ti ones for both degrees of retention.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
TESEToda.pdf (876.94 Kbytes)
Data de Publicação
2005-06-23
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.