Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.23.2009.tde-11122009-100412
Document
Auteur
Nom complet
Juliana Elston Goldman
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2009
Directeur
Jury
Aranha, Ana Cecilia Corrêa (Président)
Freitas, Patricia Moreira de
Oliveira, Marcelo Tavares de
Titre en portugais
Avaliação longitudinal da adesão à dentina irradiado pelo laser de Er,Cr:YSGG
Mots-clés en portugais
Interface adesiva
Laser de Er Cr:YSGG
Longevidade
Microtração
Resumé en portugais
O laser de Er,Cr:YSGG se apresenta como um aliado aos procedimentos minimamente invasivos. Porém, pouco se sabe sobre a longevidade da resistência de união à dentina irradiada por este equipamento. Dessa forma, o objetivo deste estudo foi avaliar a resistência de união à dentina irradiada após 90 dias de armazenamento. Para tanto, foram utilizados 64 molares humanos hígidos, que tiveram as superfícies oclusais desgastadas até a exposição de uma superfície de dentina. Esta superfície foi tratada com: abrasão com lixa SiC 600# (controle) e irradiação com o laser de Er,Cr:YSGG em 2W (90,9 J/cm2) ou 4W (181,8 J/cm2). Foram utilizados os seguintes sistemas adesivos: Adper Single Bond (3MESPE), Clearfil SE (Kuraray) ou Clearfil S3 (Kuraray), e a confecção de um bloco de resina composta Z250-3MESPE. Os dentes foram seccionados para a obtenção de palitos para o teste de microtração. Metade dos palitos foi ensaiada imediatamente, e a outra metade após 90 dias de armazenamento em água destilada. Os resultados mostraram que em todos os grupos em que foi utilizado o laser Er,Cr:YSGG apresentaram os menores valores de resistência adesiva. Com exceção do grupo controle/Clearfil S3, todos os grupos apresentaram decréscimo nos valores de resistência adesiva após os 90 dias de armazenamento. Entre os sistemas adesivos utilizados, o Single Bond apresentou os melhores valores de resistência adesiva, demonstrando maior estabilidade frente aos 90 dias de desafio/armazenamento.
Titre en anglais
Longitudinal evaluation of adherence to dentin irradiated by laser Er, Cr: YSGG.
Mots-clés en anglais
Adhesive interface
Er Cr:YSGG laser
Longevity
Microtensile
Resumé en anglais
In the minimally invasive dentistry, the Er,Cr:YSGG laser has been considered as an efficient equipment. However, little is known about the longevity of the bond strength to irradiated dentin. So, the objective of this study was to evaluate the bond strength values to laser irradiated dentin after 90 days storage. Sixty-four sound human molars were used. A flat coronal dentin surface was obtained by removing the oclusal enamel with a slow speed diamond saw. Dentin surfaces were treated with: abrasion with SiC 600# (control group) and laser irradiation with Er,Cr:YSGG in 2W or 4W. Subsequently, adhesive systems were used: Adper Single Bond (3MESPE), Clearfil SE (Kuraray) or ClearfilS3 (Kuraray). After adhesive procedures, a block of Z250-3MESPE composite resin was build up on each tooth. The teeth were sectioned in order to obtain samples for the microtensile bond strength test. Half of the samples was tested immediately, and the other half were stored for 90 days in distilled water. The results showed that all the groups in which laser was used presenter lower bond strength values. With the exception of Clearfil S3/control group, all groups showed weaker bond strength after 90 days of storage. Among all the adhesives systems used, Single Bond presented the best results, showing more stability after 90 days of storage.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2009-12-22
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.