Disertación de Maestría
DOI
https://doi.org/10.11606/D.18.2019.tde-19112019-102838
Documento
Autor
Nombre completo
Thalles Thadeu Assunção Lucas
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2019
Director
Tribunal
Gonçalves, Renato Vitalino (Presidente)
Lima, Fabio Henrique Barros de
Silva, René Alfonso Nome
Título en portugués
Estudo da formação de heterojunção e dopagem em nanotubos de TiO2: estratégias para melhorar a eficiência na fotossíntese artificial para a geração de hidrogênio
Palabras clave en portugués
Dopagem
Fotossíntese Artificial
Heterojunção
Lantânio
Nanotubos
SrTiO3
TiO2
Resumen en portugués
Desde que o experimento de Honda & Fujishima descobriu o fenômeno da fotólise da água em 1972, os pesquisadores têm procurado obter semicondutores com estrutura eletrônica de bandas apropriada para a fotossíntese artificial. Entretanto, muitos dos semicondutores mais estudados sofrem recombinação de portadores de carga que limitam a sua eficiência. Estratégias podem ser empregadas com objetivo de melhorar esses materiais, como a fabricação de nanoestruturas, heterojunção e dopagem. Neste presente trabalho, foi investigado a formação de uma heterojunção de SrTiO3 em nanotubos de TiO2, assim como a dopagem deste material com íons de lantânio. Para isso, foi anodizado o titânio metálico para obter nanotubos de TiO2, e depois modificado a sua estrutura cristalina através de reação hidrotérmica. A morfologia e cristalinidade dos nanotubos SrTiO3/TiO2 está intimamente relacionado com o tempo de reação hidrotermal. Em tempos de reação longos, o tratamento hidrotermal provoca maior formação de grãos que destrói a morfologia, enquanto em tempos curtos cria uma estruturade SrTiO3 não estequiométrica. A formação dessa estrutura foi evidenciada pela redução do band gap e vacâncias catiônicas na estrutura, observado pelas técnicas de espectroscopia UV-Vis e XPS. Não obstante, a dopagem com íons de lantânio reduz os números de defeitos cristalinos, aumentando assim a densidade de portadores de cargas. As medidas fotoeletroquimicas mostraram maior densidade de corrente quando a amostra é dopada com 10% de lantânio durante 30 minutos de tratamento hidrotermal. Esses resultados fornecem um panorama em como modificar eficientemente as estruturas 1D e como a dopagem afeta as propriedades de transporte de portadores de cargas em heterojunções produzidas por hidrotermal.
Título en inglés
Synthesis of a Heterojunction of La- SrTiO3/TiO2 nanotubes for artificial photosynthesis
Palabras clave en inglés
Artificial Photosynthesis
Doping
Heterojunction
Lanthanum
SrTiO3
TiO2
Resumen en inglés
Since Honda & Fujishima discovered the photolysis of water phenomena in 1972, researchers have been trying to obtain semiconductors materials with appropriated band structure to artificial photosynthesis. However, many semiconducting materials suffer from recombination of charge carrier that reduces their efficiency. Several strategies can be employed in order to improve these materials, such as: nanostructure fabrication, heterojunction and doping. Herein, we synthetized a heterojunction of SrTiO3 on TiO2 nanotubes, as well doping this structure with Lanthanum ions. To obtain TiO2 nanotubes, metallic titanium was anodized at room temperature. Heterojunction and doping were obtained by hydrothermal reaction. The morphology and crystallinity changed according to the hydrothermal time. In long durations, it observed an excessive grain growth, while short duration created a non-stoichiometric SrTiO3 structure. This structure was ascribed by the band gap reduction and cationic vacancies states in XPS. Nevertheless, the sample doped with lanthanum ions balanced the formation of the disordered structure, thereby increasing the charge carrier density. The photoelectrochemical measurements showed higher photocurrent density when the sample was doped with 10% lanthanum ions during 30 minutes on hydrothermal reactor. These findings provide an overview in how efficiently modify 1D structure and how the doping alters the charge carrier properties on heterojunctions produced by hydrothermal treatment.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2019-11-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.