Master's Dissertation
DOI
https://doi.org/10.11606/D.18.2014.tde-05092014-082721
Document
Author
Full name
Fábio Edson Mariani
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2014
Supervisor
Committee
Casteletti, Luiz Carlos (President)
Lombardi Neto, Amadeu
Picon, Carlos Alberto
Title in Portuguese
Tratamentos térmicos e termoquímicos de boroaustêmpera em ferros fundidos nodulares e caracterização dos produtos resultantes
Keywords in Portuguese
Austêmpera
Boretação
Cinética
Desgaste adesivo
Ferro fundido nodular
Abstract in Portuguese
Amostras de ferros fundidos nodulares ligados com Cu, Cu-Ni ou Cu-Ni-Mo foram austemperadas, boretadas e boroaustemperadas e caracterizadas quanto à dureza e o comportamento ao desgaste microadesivo, tendo sido também estudada a cinética de formação da camada. O método de boretação utilizado foi via líquida em banho de bórax fundido, com tempos de permanência de 2 e 4 horas nas temperaturas de 850, 900 e 950ºC. Procedeu-se o tratamento direto de austêmpera, a partir dessa temperatura, em banhos de sal fundidos nas temperaturas de 240, 300 e 360ºC com tempos de permanência de 4 horas (boroaustêmpera). Realizou-se também, para fins de comparação, tratamento convencional de austêmpera. Microscopias óptica e eletrônica de varredura, EDS por raios-X, testes de dureza Brinell (substrato) e Vickers (revestimento) foram realizados, bem como ensaios de desgaste microadesivo do tipo esfera presa. A boretação resultou na formação de camadas de elevadas durezas, na faixa de 1300 a 1700 HV, e elevadas resistências ao desgaste. As resistências ao desgaste das amostras boretadas ou boroaustemperadas foram aumentadas em até 40x em relação às amostras brutas de fundição ou apenas austemperadas, indicando a grande eficácia do tratamento neste tipo de propriedade.
Title in English
Boro-austempered thermal and thermochemical treatments in ductile cast iron and characterization of resulting products
Keywords in English
Adhesive wear
Austempered
Boride
Ductile cast irons
Kinetics
Abstract in English
Samples of ductile cast iron alloyed with Cu, Cu-Ni or Cu-Ni-Mo were austempered, borided and boroaustempered and afterwards characterized for hardness and micro-adhesive wear behavior. The kinetics of layer formation were also studied. The boriding method used was liquid molten borax bath, in periods of 2 and 4 hours at temperatures of 850, 900 and 950°C. The direct austempering treatment was performed from the borax bath temperature using molten salt baths at temperatures of 240, 300 and 360°C for 4 hours (boroaustempered). For comparative purposes, the conventional austempering treatment was also conducted. Optical microscopy, scanning electron microscopy, EDX, Brinell hardness measurements (substrate) and Vickers (coating) were performed, as were the tests for micro-adhesive wear. The boriding treatment resulted in the formation of layers with high hardness, in the range of 1300 to 1700 HV and high wear resistance. The wear resistance of borided or boroaustempered samples were increased by 40 times when compared to cast irons or austempered samples, indicating the high efficiency of this type of treatment in increasing the wear resistance of this material.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Mariani.pdf (5.30 Mbytes)
Publishing Date
2014-09-15
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2024. All rights reserved.