Doctoral Thesis
DOI
10.11606/T.18.2016.tde-30032016-110448
Document
Author
Full name
Julio Cesar de Souza Francisco
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2016
Supervisor
Committee
Bose Filho, Waldek Wladimir (President)
Angeloni, Mauricio
Montanari, Luciana
Sordi, Vitor Luiz
Tokimatsu, Ruís Camargo
Title in Portuguese
Resistência à propagação dúctil de trincas em aço API 5L X70 com teor de nióbio modificado
Keywords in Portuguese
Aço API 5L X70
Curvas J-R
Espécimes SE(B)
Nióbio
Tenacidade à fratura
Abstract in Portuguese
Aplicações de alto desempenho, como as de dutos utilizados no transporte de derivados de petróleo, exigem materiais com uma combinação excepcional de propriedades mecânicas, dentre as quais, elevada resistência mecânica, tenacidade e resistência à fadiga. O aço API 5L X70 com adição de nióbio apresenta-se, quando comparado com o API 5L X70 padrão, como sendo uma opção para a melhora em seu processo de fabricação, sendo sua composição química diferenciada, devido a um maior teor de nióbio. A Arcelor Mittal Tubarão tem mostrado interesse em fabricar aços API X70/X80, sem a adição de V e com adições de Nb acima do recomendado pela Petrobras. O objetivo principal deste trabalho é o estudo da resistência mecânica e de tenacidade à fratura de dois aços API 5L X70, com teores de Nb de 0,06% e Nb de 0,09% em peso, processados conforme processo HSM Arcelor Mittal Tubarão. Para o atendimento deste objetivo, serão executadas a caracterização microestrutural conforme norma ASTM E3, ensaios de tração conforme ASTM E8M e ensaios de tenacidade à fratura conforme a norma ASTM E1820 com obtenção das curvas J-R's. Foram retirados corpos de prova da região de material base, região da solda e zona termicamente afetada. A partir dos resultados obtidos observa-se que o processo de laminação controlada a quente da Arcelor Mittal, produziu microestruturas bastante similares para ambas as composições, produzindo parâmetros de resistência mecânica similares e que atenderam o especificado pela Norma API 5L X70, nível PSL2. As soldas se apresentaram, a partir de valores de dureza, ligeiramente superiores ao do metal base (overmatch), sendo o resultado de microestruturas bastante similares. Os ensaios para obtenção das curvas J-R foram capazes de apresentar resultados representativos da resistência à propagação dúctil de trinca, para as espessuras de tubos estudadas. Estes resultados indicaram elevada resistência a propagação dúctil de trinca em ambos os aços, sendo que, o MB do aço NNb apresentou resistência superior ao ANb. O MS apresentou curvas J-R bem inferiores às do MB e ZTA. Estas diferenças foram atribuídas a composição microestrutural de cada região.
Title in English
Resistance to ductile crack propagation of API 5L X70 steel modified with Nb content
Keywords in English
API 5L X70 steel
Fracture toughness
J-R curves
Niobium
Specimens SE(B)
Abstract in English
High performance applications such as pipelines used to transport oil products require materials with an exceptional combination of mechanical properties, such as high mechanical strength, toughness and fatigue resistance. The API 5L X70 steel with enhanced niobium as an option to the production of this type of HSLA steel. Arcelor Mittal, Tubarão/Brazil has great interest in producing API 5L X70/X80 steels, without V and with Nb content above the recommended by Petrobras. Thus, the main objective of this thesis is the study of the mechanical strength and fracture toughness of API 5L X70 steel with Nb content of 0.06% Nb and 0.09% by weight processed as HSM Arcelor Mittal Tubarão process. To meet this goal, microstructural characterization following the ASTM E3, tensile tests following the ASTM E8M and Elastic Plastic Fracture toughness testing, according to ASTM E1820, were carried out. Specimens were taken from the base material region, weld bead and heat affected zone. From the results obtained it was observed that the controlled hot rolling process from ArcelorMittal, produced very similar microstructures for both compositions, as a consequence similar mechanical resistance and both met the criteria specified by the API Standard 5L X70, PSL2 level. The produced girth welds presented hardness values slightly higher than those from the base metal (overmatch), and resulted in very similar microstructures. The fracture toughness tests were able to provide valid JR curves that are representative results of resistance to ductile crack propagation for this pipe thickness. Both steels presented resistance to ductile crack propagation, and that the MB of the NNB steel showed superior resistance to the ANb steel. MS showed the lowest J-R curves, while MB and ZTA presented similar behavior. These differences were attributed to microstructural composition of each region.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2016-04-05
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2019. All rights reserved.