Mémoire de Maîtrise
DOI
10.11606/D.18.2012.tde-14112012-183154
Document
Auteur
Nom complet
Aline Emanuelle Albuquerque Chemin
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2012
Directeur
Jury
Ruchert, Cassius Olivio Figueiredo Terra (Président)
Meggiolaro, Marco Antonio
Spinelli, Dirceu
Titre en portugais
Avaliação da propagação de trinca associada à corrosão da liga 7475 T7351 submetida a carregamentos de voos simulados
Mots-clés en portugais
Fadiga associada à corrosão
Ligas de alumínio
Propagação de trinca
Simulação de crescimento de trinca
Resumé en portugais
A análise da vida em fadiga em amplitude variável associada à corrosão é bastante complexa, devido a combinações entre as interações eletroquímicas ocorridas, tendo em vista a exposição da frente da trinca à névoa salina somada aos efeitos deletérios do carregamento de amplitude variável. Esta combinação de efeitos ainda não é modelada matematicamente, e os dados experimentais observados em outros trabalhos ainda geram hipóteses inconclusivas. Neste contexto, este estudo tem como objetivo avaliar a vida em fadiga da liga 7475 T7351, utilizando carregamento de voos simulados TWIST e FALSTAFF e submetida a névoa salina a 3,5 e 5%. Foram executados ensaios eletroquímicos, para verificar o potencial de corrosão dessa liga e análise microestrutural para verificar a formação de pites. O crescimento de trinca por fadiga com carregamento de voo foi simulado, sem considerar os efeitos do meio, nos programas NASGRO 4.0, AFGROW e CRACK 2000, com parâmetros calibrados no NASGRO 4.0, no intuito de verificar quais modelos matemáticos e programas descrevem a curva experimental em ar com menor erro. Os resultados mostraram que os programas NASGRO 4.0 e AFGROW se aproximaram com menor erro à curva experimental em ar. Os ensaios de crescimento de trinca por fadiga foram executados com carregamento de voos simulados e os parâmetros para o sistema de geração de névoa salina foram determinados experimentalmente. As curvas de crescimento de trinca e taxa de propagação em névoa salina foram comparadas às curvas em ar, as quais também foram obtidas sob as mesmas condições de carregamento. Observou-se que para os ensaios em névoa salina, a trinca rompeu com maior número de voos em relação às curvas em ar.
Titre en anglais
Evaluation of corrosion fatigue crack growth for 7475 T7351 alloy under spectrum loading
Mots-clés en anglais
Aluminium alloy
Corrosion fatigue
Fatigue crack growth
Fatigue crack growth simulation
Resumé en anglais
The corrosion fatigue life analysis under variable amplitude loading is very complex due electrochemistry effects in crack tip exposed to salt spray matched to harmful effects of amplitude variable loading. This effects combination is not modeling mathematically actually, and the experimentally data observed in other research generates inconclusive theories. In this context, the main aim of this research to evaluate the corrosion fatigue life of 7475 T7351 under spectrum loading TWIST and FALSTAFF and exposed to 3.5% and 5% NaCl. Electrochemistry test were performed to verify the corrosion potential followed of microstructural analysis by SEM, to verify the pitting on 7475 T7351 alloy. The fatigue crack growth was simulated, without environmental effects, using the codes NASGRO, AFGROW and CRACK 2000, the simulation parameters was fit on NASGRO 4.0, to analyze whether the crack growth models and codes are able to represent properly the air experimental crack growth data. The results showed that NASGRO 4.0 and AFGROW codes described the fatigue crack growth in air with less error. The fatigue crack growth tests were performed under spectrum loadings and the parameters to obtain salt spray were determined experimentally. The corrosion fatigue crack growth and rate data were compared to air data, under the same loading conditions. The corrosion fatigue tests showed that the specimens cracked under a larger number of flights than specimens in air.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Dissertacao.pdf (9.84 Mbytes)
Date de Publication
2012-11-21
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.