Disertación de Maestría
DOI
https://doi.org/10.11606/D.18.2007.tde-26042007-173415
Documento
Autor
Nombre completo
Jorge Rodolfo Escalante Zegarra
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2007
Director
Tribunal
Fernandes Junior, Jose Leomar (Presidente)
Barroso, Suelly Helena de Araujo
Parreira, Alexandre Benetti
Título en portugués
Avaliação de misturas produzidas com ligantes asfálticos peruanos convencional PEN 60/70 e modificados por polímero SBS tipo I 60/60 e PG 76-22
Palabras clave en portugués
Asfaltos modificados
Asfaltos peruanos
Misturas asfálticas
Polímero SBS
Resumen en portugués
Os objetivos deste trabalho são avaliar o comportamento de asfaltos peruanos convencional CAP PEN 60/70 e modificados por polímero SBS tipo I 60/60 e PG 76-22, em misturas asfálticas densas, sem e com envelhecimento em curto prazo, e estabelecer a distribuição do grau de desempenho (PG) de ligantes asfálticos com base nas condições climáticas de cada região do Peru. Para a classificação por desempenho os ligantes asfálticos procedentes de Peru foram submetidos aos ensaios convencionais e da especificação Superpave: penetração, ponto de amolecimento, viscosidade Brookfield, ponto de fulgor, retorno elástico, estabilidade a estocagem, envelhecimento em curto prazo (RTFOT), envelhecimento em longo prazo (PAV), cisalhamento dinâmico (DSR) e rigidez à fluência na flexão (BBR). Para a avaliação das propriedades mecânicas, sem envelhecimento e com envelhecimento em curto prazo, foram moldados um total de 196 corpos de prova, submetidos aos ensaios Marshall, resistência à tração, resistência à tração após umidade induzida, módulo de resiliência, fluência por compressão uniaxial estática, fluência por compressão uniaxial dinâmica e vida de fadiga. Os resultados dos ensaios mostram que o proceso de modificação dos asfaltos por polímero melhora as caracteristicas reológicas do ligante, apresentando menor índice de susceptibilidade térmica e maior resistência ao envelhecimento e melhorando o comportamento das misturas asfálticas em todos os ensaios mecânicos. Esses resultados foram confirmados pela análise estrutural com o programa computacional Elsym5, nas duas condições de envelhecimento estudadas.
Título en inglés
Evaluation of asphalt mixtures produced with conventional peruvian asphalt binder PEN 60/70 and SBS polymer-modified type I 60/60 and PG 76-22
Palabras clave en inglés
Asphalt mixtures
Modified asphalt
Peruvian asphalt
SBS polymer
Resumen en inglés
The main goal of this work is the evaluation of the behavior of conventional peruvian asphalt binder AC PEN 60/70 and SBS polymer-modified asphalts I 60/60 and PG 76-22, when used in hot-mix asphalt (HMA), under both conditions with and without short-term aging. It aims also to establish the asphalt binder performance grade (PG), which is based on the weather conditions, for different peruvian regions. The peruvian asphalt binders were submitted to conventional and Superpave laboratory tests: penetration, softening point, Brookfield viscosity, flash point, elastic recovery, storage stability, rolling thin film oven test (RTFOT), pressure aging vessel (PAV), dynamic shear rheometer (DSR) and bending beam rheometer (BBR). For the evaluation of mechanical properties 196 specimen were sumitted to Marshall, indirect tensile strength under static loading, indirect tensile strength under static loading after induced moisture, resilient modulus under dynamic diametric compression, static and dynamic creep and fatigue tests. The result show that polymer-modified asphalt binder improve rheological characteristic, in terms of thermal susceptibility and resistance to aging, and also improve the asphalt mixtures behavior, which was verified in all of the mechanical tests and after the structural analysis performed with the Elsym5 program, for all of the short-term aging conditions studied in this work.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Zegarra2007.pdf (5.53 Mbytes)
Fecha de Publicación
2007-05-03
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.