• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Dissertação de Mestrado
Documento
Autor
Nome completo
Andréa Regina Kaneko Kobayashi
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 2000
Orientador
Banca examinadora
Parreira, Alexandre Benetti (Presidente)
Ceratti, Jorge Augusto Pereira
Farias, Márcio Muniz de
Título em português
Avaliação da influência do tipo de cimento na expansibilidade de misturas de fosfogesso e cimento
Palavras-chave em português
Ataque por sulfatos
Cimento
Etringita
Expansão
Fosfogesso
Pavimento
Reciclagem
Rejeito
Resumo em português
Fosfogesso é um resíduo sólido da produção de ácido fosfórico pelas indústrias de fertilizantes. A produção anual deste material no mundo é de cerca de 180 milhões de toneladas, e isto causa problemas com a sua armazenagem. O fosfogesso tem sido estudado para uso como material de construção de bases e sub-bases de pavimentos. O fosfogesso tem pouca durabilidade frente à ação da água quando sujeito somente à estabilização mecânica. O cimento Portland é então adicionado ao fosfogesso, resultando em misturas mais estáveis. A reação do aluminato tricálcico contido no cimento e dos sulfatos presentes no fosfogesso poderia conduzir à formação de cristais de etringita e à expansão subseqüente. O objetivo desta pesquisa é avaliar a influência do tipo de cimento na expansibilidade das misturas de fosfogesso e cimento para uso na construção de pavimentos. Analisou-se o comportamento expansivo de corpos de prova compactados com diferentes proporções de fosfogesso e cimento, variando-se o tipo de cimento, energia de compactação e período de cura. Para todos os cimentos usados nesta pesquisa, considerando-se o período de 84 dias de cura, a maior parte da expansão ocorreu nos primeiros 28 dias. A influência do tipo de cimento na expansão das misturas de fosfogesso e cimento é significante, mas o teor de aluminato tricálcico não é a única explicação para o comportamento de expansão observado neste estudo, visto que os resultados experimentais indicam que quantidades crescentes de aluminato tricálcico conduzem a menores expansões, fato que contraria a expectativa inicial desta pesquisa.
Título em inglês
Evaluation of the influence of the cement type in the expansivity of cement-stabilized phosphogypsum
Palavras-chave em inglês
Cement
Ettringite
Expansion
Pavement
Phosphogypsum
Recycling
Sulfate attack
Waste
Resumo em inglês
Phosphogypsum is a solid by-product resulting from the phosphoric acid process for manufacturing fertilizers. The annual worldwide production of this material is about 180 million de tons and it causes problems with its disposal. The phosphogypsum has been studied for use in pavement base and sub-base materials. Phosphogypsum has poor durability when subjected to mechanical stabilization only in wet conditions. The addition of stabilizing materials, such as Portland cement, is one method of overcoming this deficiency. The chemical reaction between tricalcium aluminate present in Portland cement and sulfate ions supplied by phosphogypsum could lead to the formation of ettringite and subsequent expansion. The objective of this research is to evaluate the influence of Portland cement type on the expansion of cement-stabilized phosphogypsum mixtures for use as pavement construction. The expansion behavior was analyzed through compacted specimens composed by different phosphogypsum and cement proportions, varying the cement type, compaction energy and curing period. For all cements used in this research, most of expansion occurred within the first 28 days in relation to the 84 days of curing. There is a significant influence of cement type on the expansion of the cement-stabilized phosphogypsum mixtures, but the aluminate tricalcium content is not the only explanation for the expansion behavior observed in this study. The experimental results show that an increasing amount of tricalcium aluminate yields lower expansion, fact that thwarts the initial expectation of this research.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2018-01-31
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2014. Todos os direitos reservados.