Disertación de Maestría
DOI
10.11606/D.18.2016.tde-17022016-122311
Documento
Autor
Nombre completo
Ricardo Gratão Gregui
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2005
Director
Tribunal
Bose Filho, Waldek Wladimir (Presidente)
Tarpani, José Ricardo
Tokimatsu, Ruis Camargo
Título en portugués
Tenacidade à fratura dinâmica de ligas de titânio (Ti6AI4V) e de aço inoxidável (PH15-5)
Palabras clave en portugués
Aço inoxidável PH15-5
Ensaio de impacto Charpy instrumentado
Liga de titânio Ti6Al4V
Tenacidade à fratura dinâmica
Resumen en portugués
O presente trabalho visou determinar a tenacidade à fratura dinâmica, KID, primeiramente pelos conceitos da Mecânica da Fratura Elástica Linear (MFEL) e posteriormente pela Mecânica da Fratura Elasto-Plástica (MFEP), JID, em materiais que em operação podem estar sujeitos a impactos em diferentes temperaturas. Os materiais estudados, de uso na indústria aeronáutica, foram uma liga de titânio Ti6Al4V (norma SAE AMS 4911), na condição recozida e uma liga de aço inoxidável PH 15-5 (norma SAE AMS 5659), na condição H1000. Os corpos de prova pré-trincados e entalhados foram retirados nas orientações L-T e L-S, a fim de que fossem determinadas e comparadas a relação tenacidade/densidade ou tenacidade específica dos materiais estudados. Em seguida os corpos de prova foram ensaiados sob condições de carga dinâmica em uma máquina de ensaio Charpy instrumentado, marca Instron-Wolpert PW30, conforme a norma ASTM-E23, com velocidade de carregamento de 5,52 m/s e nas temperaturas de 23 e 400ºC. Os valores das tenacidades, posteriormente comparados e correlacionados, foram obtidos de acordo com as expressões matemáticas mencionadas na literatura. A razão entre as energias estimadas de iniciação (Ei) e de propagação (Ep), (Ei/Ep), foi obtida a partir dos gráficos de carga-deslocamento x tempo. A determinação e caracterização dos aspectos macro e microscópicos da fratura foram realizadas através de microscopia ótica e de varredura. Em seguida, confrontaram-se os valores e os aspectos preponderantes dos mecanismos de fratura apresentados por cada material.
Título en inglés
Dynamic fracture toughness of the titanium alloy (Ti6Al4V) and stainless steel (PH15-5)
Palabras clave en inglés
Charpy instrumented impact test
Dynamic fracture toughness
Stainless steel alloy (PH15-5)
Titanium alloy (Ti6Al4V)
Resumen en inglés
The present work aimed to evaluate the dynamic fracture toughness, KID, firstly using the Linear Elastic Fracture Mechanics parameter, (LEFM), and secondly using the Elasto-Plastic Fracture Mechanics (EPFM), JID. The materials used in this work are from aeronautic grade and are subjected to in service impact loads and temperature variation. The materials are a titanium alloy Ti6Al4V (standard SAE AMS 4911), in the annealed condition and a PH 15-5 stainless steel (standard SAE AMS 5659), H1000 condition. Both precracked and notched specimens were taken in the L-T and L-S directions, for the evaluation and comparison of the toughness/density ratio, i. e., the specific dynamic fracture toughness of the materials studied. Therefore, the specimens were tested under dynamic load using an Instron-Wolpert PW30 Instrumented Charpy Equipment, following the ASTM-E23 standard, with load speed of 5,52 m/s at 23 and 400ºC. The fracture toughness values were compared using mathematical expression from literature. The ration between the initiation (Ei) and propagation (Ep) energies, (Ei/Ep), was obtained from the load-displacement x time. The characterization of the macro and microscopic aspects of the fracture mechanisms were carried out using optical microscope and scan electronic microscope. The fracture toughness values and the fractographic observations were correlated and compared for the two materials studied.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-02-17
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.