Dissertação de Mestrado
DOI
10.11606/D.18.2013.tde-23092013-091812
Documento
Autor
Nome completo
Magda Lorena Chilito Amaya
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 2013
Orientador
Banca examinadora
Dias, Antonio Alves (Presidente)
Calil Junior, Carlito
Máscia, Nilson Tadeu
Título em português
Reforço de emendas dentadas com compósitos de fibras em peças de madeira
Palavras-chave em português
Compósitos
Curauá
Fibra de vidro
Fibras naturais
Reforço de emendas dentadas
Sisal
Resumo em português
A presente pesquisa teve como objetivo avaliar o uso de compósitos de fibras e resina epóxi no reforço de emendas dentadas em peças de madeira. Inicialmente, foi avaliada a influência da trama das fibras de sisal e de curauá sem tratamento nenhum nas propriedades mecânicas à tração dos compósitos com resina epóxi. Igualmente, foram caracterizados na tração compósitos de fibras de vidro e tecidos de sisal. Posteriormente, foi avaliada a resistência à tração paralela às fibras de peças de madeira Pinus sp em tamanho estrutural para três tipos de tratamentos: (1) peças sem emendas e sem reforço, (2) peças com emendas e sem reforço e (3) peças com emendas reforçadas por compósitos de fibras de vidro e resina epóxi. Também foram realizados testes de tração em corpos de prova isentos de defeitos com emendas dentadas usando madeira Lyptus® para três casos: (1) sem reforço na emenda, (2) reforço na emenda com fibra de vidro e (3) reforço na emenda com tecido de sisal. Os resultados da influência da trama das fibras de sisal e curauá com a resina epóxi nos testes de tração mostraram que o tipo de trama não influenciou significativamente na resistência e no módulo de elasticidade. Na caracterização dos compósitos poliméricos, a resistência do tecido de sisal foi cerca de 44% da resistência da fibra de vidro. Nas peças estruturais, devido à baixa resistência da madeira de Pinus sp utilizada, não se justificou a utilização do reforço. Nos corpos de prova isentos de defeitos de madeira Lyptus® com emendas dentadas, a eficácia do reforço foi evidenciado, com aumento de 37% na resistência à tração com reforço de fibra de vidro e de 40% com reforço de tecido de sisal, em relação aos corpos de prova isentos de defeitos sem reforço.
Título em inglês
Reinforcement finger joints with fibers composites in pieces of wood
Palavras-chave em inglês
Composites
Curaua
Fiberglass
Natural fibers
Reinforcement of finger joints
Sisal
Resumo em inglês
The present research evaluate the reinforcing of finger joints in timber pieces with composite fiber and epoxy. Initially, the influence of the weft in the tensile mechanical properties of composites using sisal fibers and curaua without any treatment was evaluated. The characterization of composites made with sisal fibers and glass fibers were also carried out. Additionally, the tensile strength parallel to the grain for pieces of Pinus sp in structural sizes for three types of treatments: (1) pieces without finger joints, (2) pieces unreinforced finger joints and (3) pieces reinforced finger joints with composite fiberglass and epoxy resin, was evaluated. Also, was evaluated the tensile strength of the finger joint test specimens Lyptus® wood for three cases: (1) unreinforced finger joint, (2) reinforced finger jointed with fiberglass and (3) reinforced finger jointed with fabric sisal. The results of influence of the weft sisal fibers and curaua with epoxy resin of tensile test showed that the weft did not significantly influence the strength and the modulus of elasticity. The characterization of polymeric composites, the strength of sisal fabric was about 44% of the fiber glass strength. The structural size pieces, the use of reinforcement it is not justified due to the low strength of the Pinus sp wood used. The test specimens of Lyptus® wood with finger joints, the efficacy of the reinforcement was evident, with 37% increase in tensile strength with glass fiber reinforcement and 40% with reinforcement sisal fabric, compared to specimens without reinforcement.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2013-09-24
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2019. Todos os direitos reservados.