Tesis Doctoral
DOI
https://doi.org/10.11606/T.18.2016.tde-18042016-113235
Documento
Autor
Nombre completo
Tatiana Bittencourt Dumêt
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2003
Director
Tribunal
Pinheiro, Libânio Miranda (Presidente)
Ducatti, Vitor Antonio
El Debs, Ana Lúcia Homce de Cresce
El Debs, Mounir Khalil
Figueiredo, Antonio Domingues de
Título en portugués
Aderência de cordoalhas em concretos de alta resistência com e sem fibras de aço
Palabras clave en portugués
Aderência
Concreto
Concreto de alta resistência
Concreto protendido
Cordoalhas
Fibras de aço
Pré-tração
Resumen en portugués
Este trabalho apresenta os resultados das investigações teórica e experimental sobre a aderência de cordoalhas pré-tracionadas, em concretos de alta resistência com e sem fibras de aço. Foram utilizadas cordoalhas de sete fios com Φp 12,7 mm e fibras de aço curtas, com ganchos nas extremidades (DRAMIX) e fator de forma 1/d=45. Foram realizados dois tipos de ensaios: arrancamento e flexão em viga. Os parâmetros estudados foram: comprimento de ancoragem (5Φp, 7Φp e 15Φp), volume de fibra (zero, 40 kg/m3 e 60 kg/m3 e grau de protensão (zero e 0,8fptk). O concreto apresentou resistências à compressão de 50 MPa no momento da transferência da protensão e 68 MPa na data de ensaio, aproximadamente. Os resultados dos dois tipos de ensaio foram analisados e comparados com as prescrições normativas da NBR 6118 (2001), da FIB Bulletin 1 (1999) e do ACI 318 (2002), onde verificou-se que as prescrições se encontram a favor da segurança. A conclusão principal resultante desta pesquisa foi que a utilização de fibras com 40 kg/'m3 por metro quadrado não influi na aderência. Já para um volume de fibra de 60 kg/'m3 por metro quadrado há um ganho de aproximadamente 28% na aderência, em relação aos concretos sem fibras de aço, nos ensaios de arrancamento. Para as vigas, não houve ganho de aderência para os volumes de fibra utilizados, nem na determinação do comprimento de transferência, nem na do comprimento de ancoragem necessário.
Título en inglés
Bond of strands embedded in plain and steel fiber reinforced high strength concrete
Palabras clave en inglés
Bond
Concrete
High-strength concrete
Prestressed concrete
Pretensioned concrete
Steel fibers
Strands
Resumen en inglés
This study presents the results of a theoretical and an experimental investigation of the bond of pretensioned strands embedded in plain and steel fiber reinforced high strength concrete. There were used seven wires strands with 12,7 mm diameter and short hooked steel fibers with an aspect ratio of 1/d=45. Two types of tests were carried out to obtain the bond characteristics of the strands: pullout tests and beam under flexure tests. The parameters studied were the volume fraction (0%, 0,51% and 0,76%) of the fibers, and the degree of prestress of the strand (zero and 0,8fptk). The concrete compressive strength was 50 MPa at transfer (3 days of age) and 68 MPa at 28 days of age (test date), approximately. The results were analyzed and compared to the provisions of the following Codes: NBR 6118 (2001) (Brazilian code under public consult), ACI-318 (2002) and FIB-Bulletin 1 (1999). The comparison indicated that the codes give a safe design. The main conclusion of this work was that the use of 0,5% of steel fibers does not influence the bond strength of the strand. The use of 0,76% of steel fibers increases the bond stress in 28% when compared with plain concrete, for the pullout tests. For the beam's tests there was no bond improvement due to the steel fibers, in both case (0,5% and (0,76%), neither for the transfer length nor for the development length.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-04-18
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.