Master's Dissertation
DOI
10.11606/D.18.1999.tde-03112003-113505
Document
Author
Full name
Adilson Roberto Takeuti
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 1999
Supervisor
Committee
Hanai, Joao Bento de (President)
Giongo, Jose Samuel
Stucchi, Fernando Reboucas
Title in Portuguese
Reforço de pilares de concreto armado por meio de encamisamento com concreto de alto desempenho.
Keywords in Portuguese
concreto de alto desempenho
encamisamento
fibras de aço
pilares
reforço
Abstract in Portuguese
Este estudo apresenta os resultados de uma investigação experimental constituída de três séries de ensaio, cada uma envolvendo dois modelos: um pilar básico de concreto armado, representando o pilar a ser reforçado e um pilar reforçado por camisa de concreto de alto desempenho com várias características. Todos os pilares básicos tinham a seção quadrada de 150 mm x 150 mm com altura de 1200 mm. Eles foram produzidos com concreto de 18 MPa de resistência nominal à compressão, armadura longitudinal com quatro barras de 8 mm de diâmetro e armadura transversal com estribos de 6.3mm de diâmetro com espaçamento de 90 mm. Os parâmetros que foram variados nas camisas de reforço foram: a) dois valores de espessura (tj); b) três valores de taxa de armadura transversal (*sw) utilizando telas soldadas ou armadura de estribos; c) adição de fibras curtas de aço. A resistência nominal à compressão do concreto utilizado em todas as camisas foi de 65 MPa, caracterizando-se portanto um concreto de alta resistência. Os pilares foram submetidos à compressão axial por meio de uma máquina hidráulica servo-controlada. Os ensaios foram realizados com controle de deslocamento, adotando-se uma velocidade de 0.005mm/s para o deslocamento do pistão. A força aplicada e as deformações continuaram sendo medidas após o alcance da força de ruína, para se avaliar o comportamento pós-pico, até se atingir uma força residual de cerca de 50% da força de pico. Modelos de cálculo da resistência última dos pilares reforçados foram analisados. Também foram testados modelos de confinamento e ductilidade para os elementos reforçados.
Title in English
Strengthening of reinforced concrete columns by means of high-performance concrete jacketing
Keywords in English
columns
high-performance concrete
jacketing
steel fiber
strengthening
Abstract in English
This study presents the results of an experimental investigation in three series of tests, each one involving two models: a basic reinforced concrete column, which represents the column to ge strengthened, and an identical basic column strengthned by a high-performance concrete jacket with variable characteristics. All the basic columns had a 150 mm x 150 mm square section and a 1,200 mm length. They were made of a 18 MPa nominal strength concrete and reinforced with four 8 mm diameter steel bars and 6.3mm diameter stirrups each. The jacket characteristics varied as follows: a) two thickness values(tj); b) three values of transverse reinforcement ratio (*sw) using welded wire steel meshes or ordinary stirrups; c) addition of short steel fibers. The nominal concrete compressive strength used in all the jackets was 65 MPa, therefore a high-strength concrete. The columns were subjected to monotonic axial compression by means of a servo-controlled hydraulic machine. A displacement increasing rate of 0.005 mm/sec at the top of the column was adopted. Load and strain measurements continued after the ultimate load to evaluate the post-peak behavior, up to a residual load-bearing capacity of about 50% of the peak load. Several calculation hypotheses were tested to evaluate the ultime strength of the rehabilitated columns. Also confinement mechanisms and ductility of the members were analyzed.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Takeuti.pdf (5.90 Mbytes)
Publishing Date
2003-12-02
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2019. All rights reserved.